Abstract:Carbon fiber reinforced polymer (CFRP) composites are commonly used for reflectors of artificial satellites operating in low earth orbit (LEO). The decay of the modulus of the CFRP composite varies under different thermal cycling environments, which can lead to a reduction in the accuracy of the reflector panels, affecting the transmission of signals. This paper investigates the impact of different thermal cycling conditions on the mechanical behavior of carbon fiber/epoxy laminated composites experimentally. Three kinds of thermal cycling conditions involving continuous temperature changes are employed to explore the influence of temperature range on the residual tensile and in-plane shear moduli of the laminates. Test results indicate that the upper temperature limit and the temperature span of the thermal cycling conditions jointly affect the mechanical properties of CFRP composite laminates, but the responses of the residual tensile and in-plane shear moduli are different under the variation of each temperature parameter alone. The residual tensile and in-plane shear moduli of the laminates under thermal cycling decrease with an expansion of the temperature span having the same upper limit. If the temperature span remains constant, an increase in the upper temperature limit leads to an increase in the residual tensile modulus, but a decrease in the residual in-plane shear modulus. The main damages causing the decay of residual tensile and in-plane shear moduli of unidirectional laminates were investigated by scanning electron microscopy (SEM) technology. Observations of the microscopic fracture of the material show that the post-curing reaction factor predominantly influences the residual tensile modulus of unidirectional laminates, while the fiber/matrix interface damage factor dominates the residual in-plane shear modulus of the unidirectional laminates. Furthermore, an increase in the fiber tensile modulus decreases both residual tensile and residual in-plane shear moduli. Notably, the residual in-plane shear modulus exhibits greater sensitivity to thermal cycling compared to the residual tensile modulus. The findings reported in this paper would provide valuable insights and guidance for the design and application of carbon fiber/epoxy composites subjected to thermal cycling conditions.

Experimental and FEM study of thermal cycling induced microcracking in carbon/epoxy triaxial braided composites

Finite Element Modeling of Thermal Cycling Induced Microcracking in Carbon/Epoxy Triaxial Braided Composites

Aging effects of carbon fiber/bismaleimide composite subjected to thermal cycling

Study on the Mechanical Performances of Carbon Fiber/epoxy Composite Material Subjected to Dynamical Compression and High Temperature Loads

Experimental and multiscale modeling investigations of cryo-thermal cycling effects on the mechanical behaviors of carbon fiber reinforced epoxy composites

Temperature Effects on Transverse Failure Modes of Carbon Fiber/bismaleimides Composites

Mechanical Properties and Internal Microdefects Evolution of Carbon Fiber Reinforced Polymer Composites: Cryogenic Temperature and Thermocycling Effects

Effects of Thermal Cycling on Damage Progress in Interlaminar-Toughened CFRP Cross-Ply Laminates

Investigation of Thermal Stress in a Unidirectional Carbon Fiber/Epoxy Resin Composite Under Thermal Cycling

Effect of Microcracks on the Tensile Properties of 3D Woven Composites

Influence of the combined effect of long hygrothermal aging and thermal cycling on mode I and II interlaminar fracture toughness of carbon/epoxy composites

Micromechanical transverse tensile crack propagation of unidirectional fiber reinforced epoxy SMC slice imbedded in a TDCB specimen

Modelling of Thermal Cracking Behaviours of Fiber-Reinforced Composites

A Microcracking-Based Model for the Dynamic Failure of Carbon/carbon Composites

Effect of heat treatment and test temperature on transverse cracking in tensile loading

Characterization on fatigue behavior and damage mechanism of C/BMI composites experienced thermal cycling

Thermal Shock Behavior of Twill Woven Carbon Fiber Reinforced Polymer Composites

Discrete Element Simulation of Transverse Cracking During the Pyrolysis of Carbon Fibre Reinforced Plastics to Carbon/Carbon Composites

On the mechanical behavior of carbon fiber/epoxy laminates exposed in thermal cycling environments

Experimental study and theoretical analysis of ECC type I fatigue fracture after subjected to sub-high temperature

Experimental Study on Compression Properties and Failure Mechanism of 3D MWK Carbon/epoxy Composites at Elevated Temperatures