Abstract:This study addressed different materials to coat iron oxide, after using co-precipitation to synthesize. During synthesizing iron oxide, FeSO4•7H2O as a single raw material , was emphasized as a precursor salt. In advance, FeSO4•7H2O was oxidized into trivalence by using hydrogen peroxide, allocated Fe(Ⅱ)and Fe(Ⅲ) mole ratio as one to two, and synthesized ferric ferrous oxide nanoparticle by sodium hydroxide co-precipitation, which TX-100 was a protective agent to disperse uniformly. Depend on the morphology of several nanopartical types through the processing, separation of precursor salt solution and NaOH solution in pump by adding TX-100 solution would get Fe3O4 ratio more evenly. Besides during the experiment, variety loading of NaOH and dispersant, using two- stage method to add NaOH as well, rod and particle mixure would obtain. XRD, SQUID, HRTEM and SEM were used to analyze the particle size, uniformity, Magnetic, and Crystal structure. Also, intend to find the relation among synthesis and properties, and continue to work on electrodes for battery application to seek the optimal performance corresponded to synthesis conditions. Preparation of Fe3O4@Ag was took AgNO3 and C6H12O6, the reductant, into Fe3O4 solution. Different mole ratio of AgNO3 and Fe3O4 were mix- coated. Through the process, surface modifier makes coating completely and uniformly. Later, same analysis entailed to Fe3O4@Ag product powder. The purpose was to examine its completely coating, thickness, and magnetism.

A Facile Bi-Phase Synthesis of Fe3O4@SiO2 Core–shell Nanoparticles with Tunable Film Thicknesses

Synthesis of Small Yolk–shell Fe3O4@TiO2 Nanoparticles with Controllable Thickness As Recyclable Photocatalysts

Synthesis and Characterization of Fe/C Core–shell Nanoparticles

Synthesis, Surface Modification and Characterization of Magnetic Fe3O4@SiO2 Core-Shell Nanoparticles

Size-controlled synthesis of Fe3O4 and Fe3O4@SiO2 nanoparticles and their superparamagnetic properties tailoring

Synthesis and characterization of Fe3O4/SiO2 core-shell nanoparticles in reverse micelles

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Synthesis of silica-coated polygonal Fe3O4 nanoparticles

A Template Method Leads to Precisely Synthesize SiO2@Fe3O4 Nanoparticles at the Hundred-Nanometer Scale

Synthesis of Monodisperse Fe@SiO2 Core-Shell Nanocapsules and Investigation of Their Magnetic Behaviour

Monodisperse Fe 3 O 4 spheres: Large-scale controlled synthesis in the absence of surfactants and chemical kinetic process

Nanostructuring silica-iron core-shell particles in a one-step aerosol process

Yolk-Shell Fe3 O4 @Void@N-Carbon Nanostructures Based on One-Step Deposition of SiO2 and Resorcinol-3-Aminophenol-Formaldehyde (R-APF) Cocondensed Resin Dual Layers onto Fe3 O4 Nanoclusters

Liquid-phase deposition of TiO2 nanoparticles on core–shell Fe3O4@SiO2 spheres: preparation, characterization, and photocatalytic activity

Synthesis and characterization of core-shell structure silica-coated Fe29.5Ni70.5 nanoparticles

Fabrication of Fe3O4@APF Magnetic Nanospheres with Tunable Core–Shell Structure: An Effective Carrier and Reducing Agent for Ag Nanoparticles

Study on the Synthesis and Application of Core-Shell Structured Nanoparticles of Fe3O4

A Facile One-Step Method to Synthesize SiO2@polydopamine Core–shell Nanospheres for Shear Thickening Fluid

Presence of urokinase‐type plasminogen activator (u‐PA) in tissue extracts of antrochoanal polyp

A Facile Strategy for the Preparation of Well-Dispersed Bimetal Oxide CuFe2O4 Nanoparticles Supported on Mesoporous Silica