An Antifreezing, Tough, Rehydratable, and Thermoplastic Poly(vinyl alcohol)/Sodium Alginate/Poly(ethylene glycol) Organohydrogel Electrolyte for Flexible Supercapacitors
Oudong Hu,Jing Lu,Guoqi Chen,Kai Chen,Jianfeng Gu,Sen Weng,Linxi Hou,Xi Zhang,Xiancai Jiang
DOI: https://doi.org/10.1021/acssuschemeng.1c02464
2021-07-15
Abstract:A hydrogel electrolyte is an ideal material for flexible energy storage equipment owing to its mechanical flexibility similar to solids and its ion transport ability analogous to liquids. However, a traditional hydrogel electrolyte cannot be remolded after forming and cannot be reused after dehydration. In addition, the traditional hydrogel electrolyte cannot work in a subzero environment. Here, the poly(vinyl alcohol)/sodium alginate/poly(ethylene glycol) (PVA/SA/PEG) organohydrogel electrolyte was successfully fabricated by a freezing–thawing process followed by soaking in a saturated NaCl aqueous solution. PEG could improve the mechanical property and endowed the organohydrogel with an excellent recyclability and healing ability. Meanwhile, PEG and NaCl in the organohydrogel also endowed the gel with low-temperature resistance. A new solution was provided to store and transport hydrogels by virtue of the good rehydration properties after the drying process. The flexible all-solid-state supercapacitor was fabricated by using activated carbon as the electrode and PVA/SA/PEG as the gel electrolyte. The flexible supercapacitors presented high areal capacitances of 103.6 mF cm<sup>–2</sup> at 2 mA cm<sup>–2</sup> at room temperature and 91.5 mF cm<sup>–2</sup> at −15 °C. It is believed that the PVA/SA/PEG organohydrogel electrolyte with outstanding flexibility, freezing resistance, recyclability, and high ionic conductivity is a promising candidate for the next-generation flexible energy storage devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c02464?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c02464</a>.Comparison of mechanical properties, calculation table of the sodium chloride content, schematic diagram of organohydrogel precursor solutions with different PEG contents, tensile properties of the gels with PEG contents of 14.3 and 28.6%, tensile properties of PVA/SA/PEG and PVA/SA gels, pictures of PVA/SA/PEG precursor solution gelling at room temperature, diagram of the change of the conductivity with the extension of soaking time, TGA curves of the gels, FTIR spectra of the gels, comparison of the mechanical properties of PVA/SA/PEG, PVA/SA/Gly, PVA/SA/EG, and PVA/SA gels, water content of the gels, rheological properties of the PVA/SA/PEG and PVA/SA/PEG-20 gels, DSC heating curves of the gels, mechanical property data of the gel after remodeling, resistance changes before and after healing, healing efficiency of the PVA/SA/PEG-20 gel, EIS curves of the original and thermally treated PVA/SA/PEG organohydrogel-based supercapacitors, GCD and CV curves of the supercapacitor at 1.3 V, electrochemical performance of the gel after remolding, capacitance retention of the supercapacitor with the PVA/SA/PEG-20 organohydrogel electrolyte at 5 mA cm<sup>–2</sup> under low temperature (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c02464/suppl_file/sc1c02464_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology