Phase Transition and Piezoelectric Properties of (1− X )(K 0.42 Na 0.58 )(nb 0.96 Sb 0.04 )O 3 – X (bi 0.5 Na 0.5 ) 0.90 Mg 0.10 ZrO 3 Lead-Free Ceramics
Jiagang Wu,Yingjuan Yang,Xiaopeng Wang,Dingquan Xiao,Jianguo Zhu
DOI: https://doi.org/10.1007/s10854-014-2218-2
2014-01-01
Journal of Materials Science Materials in Electronics
Abstract:(1−x)(K0.42Na0.58)(Nb0.96Sb0.04)O3–x(Bi0.5Na0.5)0.90Mg0.10ZrO3 [(1−x)KNNS–xBNMZ] lead-free ceramics have been prepared by the normal sintering, and effects of BNMZ content on their phase structure, microstructure, and electrical properties have been systematically investigated. These ceramics with 0.045 ≤ x ≤ 0.05 possess a rhombohedral–tetragonal (R–T) phase boundary, as confirmed by the temperature dependence of dielectric properties and X-ray diffraction patterns. The grain size of the ceramics first increases and then decreases as the BNMZ content increases, and the ceramic with x = 0.06 possesses much smaller grains (<1 μm), resulting in the abnormal electrical and phase transition behavior. In addition, the Mg2+ was homogenously distributed in the ceramic matrixes. These ceramics with R–T phase boundary show enhanced dielectric, ferroelectric, and piezoelectric properties as compared with a pure KNN, and optimum electrical properties (e.g., P r ~ 16.23 μC/cm2, E C ~ 7.58 kV/cm, ε r ~ 2,663, tan δ ~ 0.034, d 33 ~ 434 pC/N, k p ~ 0.47, and T C ~ 244 °C) were found in the ceramic with x = 0.0475. We believe that the (1−x)KNNS–xBNMZ ceramic is a promising candidate for lead-free piezoelectric devices.