Balanced development of piezoelectricity and Curie temperature in (1 − <Emphasis Type="Italic">x</Emphasis>)K<Subscript>0.44</Subscript>Na<Subscript>0.52</Subscript>Li<Subscript>0.04</Subscript>Nb<Subscript>0.96</Subscript>Sb<Subscript>0.04</Subscript>O<Subscript>3</Subscript>–<Emphasis Type="Italic">x</Emphasis>Bi<Subscript>0.25</Subscript>Na<Subscript>0.25</Subscript>Ba<Subscript>0.5</Subscript>ZrO<Subscript>3</Subscript> lead-free piezoelectric ceramics

Zhi-Xue Xu,Jian-Min Yan,Lei Guo,Meng Xu,Fei-Fei Wang,Yu-Kuai Liu,Ren-Kui Zheng

DOI: https://doi.org/10.1007/s10854-017-8040-x

2018-01-01

Abstract:(1 − x)K0.44Na0.52Li0.04Nb0.96Sb0.04O3–xBi0.25Na0.25Ba0.5ZrO3 [(1 − x)KNLNS-xBNBZ] (0 ≤ x ≤ 0.05) lead-free piezoelectric ceramics were prepared by using the conventional solid-state reaction method. The relationships among the composition, phase structure, phase volume fraction, microstructure, dielectric, ferroelectric, and piezoelectric properties as well as the phase diagram are established. Rietveld refinements of X-ray diffraction patterns show that with increasing doping level the volume fractions of the orthorhombic and tetragonal phases evolve from 58.7 and 41.3% for x = 0 to 1.7 and 98.3% for x = 0.05, which has strong impacts on the piezoelectric coefficient d 33 and Curie temperature T C. Upon the doping of BNBZ an orthorhombic-tetragonal (O–T) phase boundary forms near room temperature, resulting in an optimum d 33 ~ 288 pC/N, T C ~ 305 °C, a converse piezoelectric coefficient d 33 * ~ 391 pm/V, and a field-induced strain S ~ 0.156% for the x = 0.035 ceramics. These results demonstrate that a balanced development of d 33 and T C can be realized by choosing suitable doping materials and content.