Multi‐Phase Morphology with Enhanced Carrier Lifetime via Quaternary Strategy Enables High‐Efficiency Thick‐Film and Large‐Area Organic Photovoltaics
Lingling Zhan,Shouchun Yin,Yaokai Li,Shuixing Li,Tianyi Chen,Rui Sun,Jie Min,Guanqing Zhou,Haiming Zhu,Yiyao Chen,Jin Fang,Chang‐Qi Ma,Xinxin Xia,Xinhui Lu,Huayu Qiu,Weifei Fu,Hongzheng Chen
DOI: https://doi.org/10.1002/adma.202206269
IF: 29.4
2022-09-16
Advanced Materials
Abstract:With the continuous breakthrough of organic photovoltaics (OPVs) efficiency, their practical applications are on the agenda. However, the thickness tolerance and upscaling in recently reported high‐efficiency devices remains challenging. In this work, the multi‐phase morphology and desired carrier behaviors were realized by utilizing the quaternary strategy. Notably, the exciton separation, carrier mobility, and carrier lifetime are enhanced significantly, the carrier recombination and the energy loss (Eloss) is reduced, thus beneficial for the higher short‐circuit density (JSC), fill factor (FF) and open‐circuit voltage (VOC) of the quaternary system. Moreover, the intermixing‐phase size was optimized, favorable for constructing the thick‐film and large‐area devices. Finally, the device with 110 nm thick active layer shows an outstanding PCE of 19.32% (certified 19.35%). Furthermore, the large‐area (1.05 cm2 and 72.25 cm2) devices with 110 nm thickness present PCEs of 18.25% and 12.20%, and the device with 305 nm thick film (0.0473 cm2) delivers a PCE of 17.55%, which are among the highest values reported. Our work demonstrates the potential of quaternary strategy for large‐area and thick‐film OPVs and promotes the practical application of OPV in the future. This article is protected by copyright. All rights reserved
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology