Anisotropic plastic deformation behavior of B2-ordered Fe3Al single crystals at room temperature

郑为为,杨王yun,WW Zheng,WY Yang,ZQ Sun

IF: 3.752

2002-01-01

Transactions of Nonferrous Metals Society of China

Abstract:The tensile plastic deformation behavior of B2-ordered Fe3Al single crystals at room temperature was systematically investigated. The results show that the mechanical properties are strongly orientation dependent. The plastic elongation of crystals with orientation near [110] is as high as 42 %. Slip trace analysis shows that although slip planes are found to change among [110], [112] and [123] with the change in orientations, the initial slip planes in all cases are [110], Five-stage work hardening curve including four linear stages and one parabolic stage is obtained; but not all stages are observed in the actual deformation of each crystal. In combination with investigations of dislocation substructure, it is found that deformations in stage I similar to M are corresponding to the motion of two-fold superdislocations. The higher work hardening rate of stage H is mainly due to the stronger interactions between primary dislocations and secondary dislocations than those in stage III. Deformation in stage IV involved is not only the motion of two-fold superdislocations but also the slip of dissociated superpartials with APB traps and the formation of APB tube, both of which are attributed to the hardening. Deformation in stage V is controlled by the cross slip of dissociated superpartials. The dominated softening effect of cross slip reduces the hardening rate and leads to the formation of parabolic stage.