Arrest of Intergranular Corrosion in Austenitic Stainless Steel by Twin-induced Grain Boundary Engineering(Student Poster Session)

Masayuki Shimada,Hiroyuki Kokawa,Zhan Jie Wang,Yutaka S. Sato
DOI: https://doi.org/10.1299/jsmeatemapcfs.2.01.03.0_1036
2001-01-01
Proceedings of the Asian Pacific Conference on Fracture and Strength and International Conference on Advanced Technology in Experimental Mechanics
Abstract:Sensitization by chromium depletion due to chromium carbide precipitation at grain boundaries in austenitic stainless steels can not be prevented perfectly only by existing conventional techniques, such as reduction of carbon content, stabilization-treatment, local solution-heat-treatment, etc. In this investigation, a thermomechanical treatment was tried to improve the resistance to the sensitization by grain boundary engineering (GBE). A type 304 austenitic stainless steel was cold-rolled and solution-heat-treated, and then sensitization-heat-treated. The grain boundary character distribution was examined by orientation imaging microscopy (OIM). The intergranular corrosion resistance was evaluated by electrochemical potentiokinetic reactivation (EPR) and ferric sulfate-sulfuric acid tests. The sensitivity to intergranular corrosion was reduced by the thermomechanical treatment and indicated a minimum at a small roll-reduction. The frequency of coincidence-site-lattice (CSL) boundaries indicated a maximum at the small reduction. The ferric sulfate-sulfuric acid test showed much smaller corrosion rate in the thermomechanical-treated specimen than in the base material. A high density of annealing twins were observed in the thermomechanical-treated specimen. The results suggest that the thermomechanical treatment can introduce low energy segments in the grain boundary network by annealing twins and can arrest the percolation of intergranular corrosion from the surface.
What problem does this paper attempt to address?