Synthesis, crystal structure and photoluminescence of novel blue-emitting Eu2+-doped (SiC)x–(AlN)1−x phosphors by a nitriding combustion reaction

zhongqi shi,zhilei wei,cheng he,ruifeng jing,hongjie wang,guanjun qiao

DOI: https://doi.org/10.1039/c4ra11277f

IF: 4.036

2014-01-01

RSC Advances

Abstract:Novel blue-emitting phosphors with the chemical composition of (SiC)(x)-(AlN)(1-x):yEu(2+)(x = 0.06-0.50, y = 0.001-0.01) were synthesized by a nitriding combustion reaction route, and the crystal structure, luminescence properties and thermal stability of the (SiC)(x)-(AlN)(1-x):yEu(2+) phosphors were investigated by theoretical and experimental approaches. First-principles calculation results prove that the solid solution of SiC with AlN promotes the doping of Eu2+ ions into the (SiC)(x)-(AlN)(1-x) host lattice, and Eu2+ ions tend to occupy Al sites of the host. The synthesized (SiC)(x)-(AlN)(1-x):yEu(2+) phosphors absorb light in the region of 250-425 nm and show a single and symmetric broadband emission centered at about 470 nm due to the 4f(6)5d-4f(7) transitions of Eu2+. The luminescence intensity increases with the SiC content and reaches its maximum at x = 0.20. The critical quenching concentration of Eu2+ in the (SiC)(0.20)-(AlN)(0.80): yEu(2+) phosphor is about y = 0.006. The composition-optimized (SiC)(0.20)-(AlN)(0.80):0.006Eu(2+) phosphor shows a small thermal quenching, retaining the luminance of 91.1% at 150 degrees C. The CIE coordinates were measured as (0.135, 0.167) with high color purity. The above results indicate that (SiC)(x)-(AlN)(1-x):yEu(2+) is a promising candidate as a blue-emitting ultraviolet convertible phosphor for white LEDs, and the combustion reaction route is expected to be applicable to the synthesis of other kinds of nitride phosphors.