Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Electrospinning Fabrication of Polycrystalline LaCrO3 Porous Hollow Nanofibers

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

LaMnO3 and La0.875Sr0.125MnO3 Nanofibers via Electrospinning

LaMnO_3 and La_(0.875)Sr_(0.125)MnO_3 Nanofibers via Electrospinning

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Synthesis and optical properties of chromium-doped spinel hollow nanofibers by single-nozzle electrospinning

Electrospinning-based preparation of LaMO3(M=Co Fe Mn) nanofibers and its characterization

Fabrication of Mn2O3 nanowire with ultra fine morphology via an electrospinning technology

Synthesis of La2NiO4+δ Nanofibers by Electrospinning Method and Their Application

Electrochemical and DFT investigations of light rare earth chromite nanofibers

Nanostructured LiCoO2 and LiMn2O4 fibers fabricated by a high frequency electrospinning

Nanofibers of LiMn2O4 by electrospinning

Fabrication and optical properties of Y2O3: Eu3+ nanofibers prepared by electrospinning.

Fabrication and characterization of FePt magnetic nanofibers via electrospinning technique

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Highly Enhanced Electrical Conductivity in Electrospun La9.6Si6O26.4 Nanofibres

Fabrication of dense and porous Li2ZrO3 nanofibers with electrospinning method

Fabrication of Cuprate Superconducting La1.85sr0.15cuo4 Nanofibers by Electrospinning and Subsequent Calcination in Oxygen

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Structure and magnetic properties of electrospun rare earth orthochromites nanofibers