Effect of Heat Treatment on Microstructure and Properties of Wear Resistant Cast Fe-C-B Alloy

SONG Xu-ding,FU Han-guang,YANG Jun

2008-01-01

Abstract:The microstructure and properties of cast Fe-C-B alloy containing 0.5%～2.0 wt%B and lower than 0.2 wt%C after heat treatment were investigated by means of optical microscopy(OM),scanning electron microscopy(SEM),transmission electron microscopy(TEM) and wear test.The results show that the solidification microstructure of the cast Fe-C-B alloy consists of Fe_2B type boride and pearlite and ferrite matrix.The distribution of borides is in the form of fishbone and network.After water quenching at 950～1100℃ and tempering at 200℃,the broken boride network is observed and the matrix transforms to lath martensite in the alloy.When the quenching temperature increases,more broken borides are found,and there is a few plate martensite in the matrix.Hardness of the cast Fe-C-B alloy after heat treatment is 55～60 HRC,its impact toughness and fracture toughness are more than 10 J/cm~2 and 30 MPa·m~(1/2),respectively.Using 120 mesh quartz as abrasive,the wear resistance of cast Fe-C-B alloy under abrasive wearing is higher than that of high manganese steel and slightly lower than that of high chromium white cast iron.