Comparing the Role of Zr and Hf Atoms on Microstructure and Mechanical Properties Optimization of Ti2AlN Reinforced Ti48Al 0.5W Composites
Siyu Chen,Yingmei Tan,Xuan Wang,Feng Cao,Liang Wang,Yanqing Su,Jingjie Guo
DOI: https://doi.org/10.1016/j.jallcom.2022.168159
IF: 6.2
2023-01-01
Journal of Alloys and Compounds
Abstract:In order to further optimize the mechanical properties of TiAl composites, Ti2AlN/Ti48Al0.5W composites with 1 at% Zr/Hf addition were prepared by arc melting, which were termed as Base alloy, Zr-containing alloy and Hf-containing alloy. The grain size, element distribution, phase content and compressive prop-erties were investigated and compared in this work. With 1 at% Zr/Hf addition, the lamellae colony size decreased from 33 mu m to 25/23 mu m, and Zr atoms almost dissolved into the single gamma phase in the form of solid solution atoms, while Hf atoms distributed in both alpha 2/gamma lamellae and single gamma phase, and part Hf atoms also existed in the form of B2 phase, which illustrated the higher solid solution of Zr atoms in TiAl com-posites comparing with Hf atoms. The gamma phase content increased and the alpha 2 phase content decreased, especially with 1 at% Zr addition, which acted as gamma-phase stabilizing element. With 1 at% Hf addition, the compressive strength and strain increased from 2010 to 2221 MPa and from 23.9 % to 26.2 %, respectively, which was attribute to the solid solution strengthening of Hf atoms by substituting Ti atoms, refinement of alpha 2/gamma lamellae and increased gamma phase content. Compared with 1 at% Hf addition, 1 at% Zr addition led to higher compressive strength and strain, which were 2344 MPa and 26.8 %, respectively, and this result was due to the higher concentration of Zr atoms in gamma phase and higher content of gamma phase. On account of density, cost and performance, Zr atoms are more suitable as an alloying element to further optimize the micro-structure and mechanical properties of TiAl composites. (c) 2022 Elsevier B.V. All rights reserved.