In-situ conversion of Bi2O2CO3 to Bi2O2CO3/Fe2O3/BiOCl, Fe2O3/BiOCl heterojunctions and boosted photodegradation activity
Zhe Liu,Chen Yuan,Weiyi Hao,Zilin Lu,Jiawei Zhang,Wansheng Ruan,Ben Ma,Wenjun Jiang,Fei Teng
DOI: https://doi.org/10.1016/j.inoche.2021.109066
IF: 3.428
2021-12-01
Inorganic Chemistry Communications
Abstract:In this work, the ternary Bi2O2CO3/Fe2O3/BiOCl (BOC/Fe2O3/BiOCl) and binary Fe2O3/BiOCl heterojunctions are synthesized by an in-situ hydrothermal method. It is found that the addition amount of FeCl3 has a great influence on the formation of multiple heterojunctions. The XRD and HRTEM results illustrate that the formation of multiple heterojunctions. At FeCl3: BOC = 0.1–0.8:1 (molar ratio), the BOC/Fe2O3/BiOCl ternary heterojunction has formed (S1 0.1Fe-BOC-S5 0.8Fe-BOC). At FeCl3: BOC = 1: 1 and 2.5: 1 (molar ratio), the Fe2O3/BiOCl binary heterojunction has formed (S6 1Fe-BOC, S7 2.5Fe-BOC). Besides, under ultraviolet light irradiation (λ < 400 nm), the photocurrents of S4 0.7Fe-BOC, S5 0.8Fe-BOC, S6 1Fe-BOC and S7 2.5Fe-BOC are 4, 3, 6 and 5 times higher than that of BOC, respectively suggesting the greatly improved charge transfer and separation efficiency. Under ultraviolet light irradiation (λ < 400 nm) within 20 min, ∼40% of rhodamine B (RhB) are photodegraded by S4 0.7Fe-BOC and S5 0.8Fe-BOC, ∼65% of RhB are photodegraded by S6 1Fe-BOC and S7 2.5Fe-BOC. While 8% and 2% of RhB are photodegraded by S1 0.1Fe-BOC and BOC within 20 min, respectively. The apparent reaction kinetic rate constant (ka ) for S1 0.1Fe-BOC (0.024 min−1), S4 0.7Fe-BOC (0.082 min−1), S5 0.8Fe-BOC (0.086 min−1), S6 1Fe-BOC (0.127 min−1) and S7 2.5Fe-BOC (0.093 min−1) are 2.7, 9.1, 9.6, 14.1 and 10.3 times as high as that of BOC (0.009 min−1), respectively. The higher photocatalytic activity of the composite is mainly due to the heterojunction formation, which efficiently improves charge separation and favors the generation of superoxide radical ( O2 –) and hydroxyl radical ( OH). This work provides a simple in-situ hydrothermal method to fabricate multiple heterojunctions with the obviously boosted photoactivity.
chemistry, inorganic & nuclear