Fabrication of microsphere-like Bi3O4Cl/BiOI Z-scheme heterostructure composites and its enhanced photocatalytic performance for degradation of MO and RhB

Liangliang Cheng,Xinyan Xiao,Yi Wang,Mingli Lu

DOI: https://doi.org/10.1007/s11164-020-04231-7

IF: 3.134

2020-08-10

Research on Chemical Intermediates

Abstract:Microsphere-like Bi₃O₄Cl/BiOI Z-scheme heterostructure photocatalysts with improved photocatalytic performance were synthesized by hydrothermal method. SEM images showed that Bi₃O₄Cl had morphological regulation effect on BiOI, which could greatly increase the active sites of the composites. And a possible process for the change of morphology was put forward. Two dyes with different charging properties (MO and RhB) were selected to evaluate the activities of the prepared photocatalysts. As a consequence, the 10%Bi₃O₄Cl/BiOI composite showed 99.8% of the degradation efficiency for MO degradation in 90 min of simulated sunlight irradiation, the degradation rate constant (0.0577 min⁻¹) was 28.9 and 5.5 times higher than that of pure Bi₃O₄Cl and BiOI, respectively. Similarly, the 10%Bi₃O₄Cl/BiOI composite had more superior photocatalytic performance than pure Bi₃O₄Cl and BiOI. The enhancement of photocatalytic performance was mainly attributed to the increased light absorption, charge separation efficiency and specific surface area, which was proved by DRS, PL, EIS and N₂ adsorption–desorption characterizations. Further, the radical trapping experiments confirmed that holes (h⁺) and superoxide radicals (^<b>·</b>O₂⁻) were the main active species for the photodegradation. Combining with the DRS and trapping experiments, a possible Z-scheme heterojunction photocatalytic mechanism was proposed.

chemistry, multidisciplinary