Probing of bonding changes in B[subscript 2]O[subscript 3] glasses at high pressure with inelastic X-ray scattering

Sung Kuen Lee,Peter J. Eng,Ho-kwang Mao,Yue Meng,Matthew Newville,Michael Y. Hu,Jinfu Shu,CIW

IF: 41.2

2010-01-01

Nature Materials

Abstract:Full understanding of atomic arrangement in amorphous oxides both at ambient and high pressure is an ongoing fundamental puzzle. Whereas the structures of archetypal oxide glasses such as v-B{sub 2}O{sub 3} at high pressure are essential to elucidate origins of anomalous macroscopic properties of more complex melts, knowledge of the high-pressure structure and pressure-induced coordination changes of these glasses has remained elusive due to lack of suitable in situ experimental probes. Here, we report synchrotron inelastic X-ray scattering results for v-{sub 2}O{sub 3} at pressures up to 22.5 GPa, revealing the nature of pressure-induced bonding changes and the structure. Direct in situ measurements show a continuous transformation from tri-coordinated to tetra-coordinated boron beginning at 4-7 GPa with most of the boron tetra-coordinated above 20 GPa, forming dense tetrahedral v-B{sub 2}O{sub 3}. After decompression from high pressure the bonding reverts back to tri-coordinated boron but with the data suggesting a permanent densification.