Abstract:In the present contribution, ultrafine fibers were spun from poly(vinyl alcohol) (PVA)/water solution using a homemade electrospinning set-up. The effects of the concentration of polymer solution, spinning voltage and collection distance between the tip to target on the morphological appearance and average diameter of the as-spun PVA fibers were investigated. A more comprehensive and systematic understanding of process parameters of the electrospinning was obtained. In this experiment fibers with diameter ranging from 100 nm to 1000 nm were obtained. The results showed that the solution concentration significantly affected the morphology and diameters of the as-spun PVA fibers. Lower concentration tended to facilitate the formation of fibers with beads. With increasing solution concentration, the morphology was changed from beaded fiber to smooth and uniform fiber and the fiber diameter was increased. Spinning voltage also had an important influence on the diameters of fibers, while the collection distance slightly affected the diameters of fibers. Thinner fibers were received on the target with lower voltage applied on the nozzle. The morphology of fibers electrospun from PVA was observed and analyzed by scanning electron microscopy (SEM).

Electrospun Alumina Nanomicro Fibers from Aluminum Nitrate/PVA Precursor

Alumina (al2o3) Nanofibers from Electrospinning

Alumina (<i>Al<sub>2</sub>O<sub>3</sub></i>) Nanofibers from Electrospinning

Electrospinning Preparation and Characterization of Alumina Nanofibers with High Aspect Ratio

Fabrication of Cr<sub>2</sub>O<sub>3</sub>/Al<sub>2</sub>O<sub>3</sub> composite nanofibers by electrospinning

Fabrication of Cr 2 O 3 /Al 2 O 3 composite nanofibers by electrospinning

Fabrication of Polyvinylpyrrolidone/Boehmite Nanofibers by Electrospinning

Preparation and Characterization of LaAlO3 Nanofibers Via Electrospinning

Preparation of Y3Al5O12 nanofibres by electrospinning

Fabrication of Mn2O3 nanowire with ultra fine morphology via an electrospinning technology

Electrospinning of Silver/Sodium Alginate/Poly(vinyl Alcohol) Fibers

Insights into the pore-forming effect of polyvinyl butyral (PVB) as the polymer template to synthesize mesoporous alumina nanofibers via electrospinning

Preparation of Α-Fe2o3 Nanofiber Via Electrospinning Process

Fabrication of Flexible Alpha-Alumina Fibers Composed of Nanosheets

Electrospinning Preparation of LaFeO 3 Nanofibers

Microstructural Differences Between Electrospun Alumina Borate Nanofibers Prepared by Solutions with Different Pvp Contents

Preparation Of Alnps/Nc Composite Nanofibers By Electrospinning

Preparation and Properties of Poly (vinyl Alcohol) Nanofibers by Electrospinning

Electrospun LaAlO3 nanofibers from different solvent systems

Preparation of Mn2O3 and Mn3O4 nanofibers via an electrospinning technique