Abstract:In this study, the crystalline morphology and mechanical property of Olefin Block Copolymer (OBC) were tailored by adding a small amount (up to 10 wt%) of ultrahigh molecular weight polyethylene (UHMWPE). To do this, OBC and UHMWPE was solution blended first and then subjected to compression molding or injection molding, respectively. It was found that a small quantity of UHMWPE (0.5 wt%, 1 wt %) can be fully mixed with OBC, while phase separation occurs when UHMWPE content is higher than 2.5 wt%, as suggested by SEM and DSC results. For compression molded samples, an obvious increase of Young's modulus from 12 MPa to 22 MPa while maintaining the good elasticity of OBC was observed as the content of UHMWPE is less than 2.5 wt% (in the phase miscible range). With further increasing of UHMWPE content to 10 wt%, only slightly increased Young's modulus is seen. Thus the miscibility between OBC and UHMWPE plays an important role in determining the mechanical property for compression molded samples. However, a continuous increase of Young's modulus was observed with the increase of UHMWPE content for samples obtained via injection molding, with a slight increase (from 23 MPa to 40 MPa) as the content of UHMWPE is less than 2.5 wt%, while with a large increase (from 40 MPa to 156 MPa) as the content of UHMWPE increases from 2.5 wt% to 10 wt, accompanied with a greatly decrease of elongation (from 1100% to 50%). Even elastomer-to-plastic transition takes place when the content of UHMWPE is large (5 wt%, 10 wt%). Structural analysis of injection-molded samples shows that shish-kebab-like structures can be successfully induced as addition of UHMWPE along with gradually increased crystal orientation. It was interesting to find that small-addition of UHMWPE favors increased tie-effect due to the miscibility between OBC and UHMWPE, which is helpful to the elasticity retaining as well as strength enhancement, while large-addition of UHMWPE gives rise to phase separation and mixed shish-kebabs (OBC/UHMWPE hybrid shish-kebabs and UHMWPE homo-shish-kebabs), leading to elastomer-to-plastic transition. (C) 2016 Elsevier Ltd. All rights reserved.

Improved Performance Balance of Polyethylene by Simultaneously Forming Oriented Crystals and Blending Ultrahigh-Molecular-Weight Polyethylene

Tailored Bonded Interfacial Intermolecular Entanglement of Polyethylene/Ultrahigh-Molecular-Weight Polyethylene Blends: Enhancing Miscibility, Reinforcement, and Friction Reduction

Constructing Highly Oriented and Condensed Shish-Kebab Crystalline Structure of HDPE/UHMWPE Blends Via Intense Stretching Process：achieving High Mechanical Properties and In-Plane Thermal Conductivity

Constructing highly oriented and condensed shish-kebab crystalline structure of HDPE/UHMWPE blends via intense stretching process:Achieving high mechanical properties and in-plane thermal conductivity

Morphology evolution and mechanical property enhancement of linear low‐density polyethylene by adding disentangled ultrahigh molecular weight polyethylene

Short-time fabrication of well-mixed high-density polyethylene/ultrahigh-molecular-weight polyethylene blends under elongational flow: morphology, mechanical properties and mechanism: Fabrication and performance of HDPE/UHMWPE blends under elongational flow

Ultra-high molecular weight polyethylene (UHMWPE)/high-density polyethylene (HDPE) blends with outstanding mechanical properties, wear resistance, and processability

Melt Processing and Structural Manipulation of Highly Linear Disentangled Ultrahigh Molecular Weight Polyethylene

Dynamic rheological behavior, crystallization and friction performance of ultrahigh molecular weight polyethylene/polypropylene blends by multi-step melt processing strategy

In Situ Synthesized Self-Reinforced HDPE/UHMWPE Composites with High Content of Less Entangled UHMWPE and High Gradient-Distributed Oriented Structures

Fabrication Of Well-Miscible And Highly Enhanced Polyethylene/Ultrahigh Molecular Weight Polyethylene Blends By Facile Construction Of Interfacial Intermolecular Entanglement

Rheological and Mechanical Properties of Ultrahigh Molecular Weight Polyethylene/high Density Polyethylene/polyethylene Glycol Blends

Tailoring the Crystalline Morphology and Mechanical Property of Olefin Block Copolymer Via Blending with a Small Amount of UHMWPE

Hierarchical structure manipulation of UHMWPE/HDPE fibers through in-reactor blending with Cr/V bimetallic catalysts

Realizing Mechanically Reinforced All-Polyethylene Material by Dispersing UHMWPE Via High-Speed Shear Extrusion

Effects of Different Ultrahigh Molecular Weight Polyethylene Contents on the Formation and Evolution of Hierarchical Crystal Structure of High‐density Polyethylene/ultrahigh Molecular Weight Polyethylene Blend Fibers

Exploring the Entangled State and Molecular Weight Ofuhmwpeon the Microstructure and Mechanical Properties Ofhdpe/uhmwpeblends

Effects of Maleic Anhydride Grafted Polyethylene on Rheological, Thermal, and Mechanical Properties of Ultra High Molecular Weight Polyethylene/Poly(Ethylene Glycol) Blends

Synergic Enhancement of High-density Polyethylene Through Ultrahigh Molecular Weight Polyethylene and Multi-flow Vibration Injection Molding: A Facile Fabrication with Potential Industrial Prospects

Enhancing Chain Mobility of Ultrahigh Molecular Weight Polyethylene by Regulating Residence Time under a Consecutive Elongational Flow for Improved Processability

Elongational Flow Field Processed Ultrahigh Molecular Weight Polyethylene/Polypropylene Blends with Distinct Interlayer Phase for Enhanced Tribological Properties