Abstract:Aim: To explore the degradation characteristics of composite of calcium polyphosphate fiber (CPPF), calcium phosphate cement (CPC) and micromorselized bone in vitro. Methods: The experiment was conducted in the Central Laboratory of Animal Experiment of the First Hospital Affiliated to Harbin Medical University from February to October 2005. 1 The rabbit iliac bone was made into micromorselized bone with the diameter of 300-500 μm. 2 Two groups of biochemical composite were made respectively according to the mass-ratios of CPPF/CPC/micromorselized bone at 1:4:4 (CPPF group/CPC group/micromorselized bone group) and that of CPC/micromorselized bone at 1:1 (CPC group/micromorselized bone group). 3 The porosity was calculated by studying the pore diameter of composite under scanning electron microscope. 4 In vitro experiment of degradation, two groups of composite were put into the phosphate buffered solution (PBS) (pH 7.4) respectively to study the changes in weight-loss ratio of composite in degradation liquid as well as the changes in pH value of degradation liquid and the biomechanical changes in composite at different time-points. Results: 1 Changes in porosity, pH value and mass of degradation of both kinds of composites: The porosity of composite of CPPF/CPC/ micromorselized bone was 72.1% with the pore diameter of 100-400, and the pH value was constant while degradation. The mass changed little within 4 weeks and decreased rapidly after the 4th week, which was 50% of the initial mass in the 12th week. The porosity of compound materials of CPC/micromorselized bone was 58.2% and was 50-300 μm in the gap diameter with slight changes in pH value, and the mass changed little within 6 weeks, which decreased rapidly after 6 week, and was 70% of the initial mass in the 12th week. 2 Biomechanical changes in composite of two groups in the degradation: the primary biomechanical strength was 9.28 MPa in CPPF/CPC/micromorselized bone and was 6.21 MPa in CPC/ micromorselized bone, and there was significant difference between them (P< 0.05). The strength of CPPF/CPC/micromorselized bone decreased slowly within 4 weeks, then decreased obviously after 4 weeks, which was 0.18 MPa in the 12th week, while the strength of CPC/micromorselized bone decreased symmetrically and was 0.24 MPa in the 12th week. Conclusion: The composite of CPPF/CPC/micromorselized bone is a new bone repair material, which is suitable for bone tissue engineering for its good characteristics of porosity, pore diameter and degradation.

Preparation and Degradation Performance of Ca/Mg/PO_4 Bone Repair Materials

Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

Influence of Monocalcium Phosphate on the Properties of Bioactive Magnesium Phosphate Bone Cement for Bone Regeneration

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

Improvement of the mechanical properties and corrosion resistance of biodegradable β-Ca3(PO4)2/Mg-Zn composites prepared by powder metallurgy: the adding β-Ca3(PO4)2, hot extrusion and aging treatment

Composition control in biphasic silicate microspheres on stimulating new bone regeneration and repair of osteoporotic femoral bone defect

Investigation on the In Vitro Degradation and Release Behaviors of Calcium Phosphate Containing Chinese Medicine

Study on the degradation of hydroxypropyl methylcellulose‐modified magnesium phosphate cement in different solutions

Development of Magnesium Calcium Phosphate Biocement for Bone Regeneration

Characterization and Degradation Study of Calcium Phosphate Coating on Magnesium Alloy Bone Implant in Vitro

Degradability and Osteogenesis of Mesoporous Magnesium Silicate Modified Calcium Sulphate Bone Cement

Self-Healing Micro Arc Oxidation and Dicalcium Phosphate Dihydrate Double-Passivated Coating on Magnesium Membrane for Enhanced Bone Integration Repair

Preparation and properties of porous calcium phosphate ceramic microspheres modified with magnesium phosphate surface coating for bone defect repair

Effects of Mesoporous Calcium Magnesium Silicate on Setting Time, Compressive Strength, Apatite Formation, Degradability and Cell Behavior to Magnesium Phosphate Based Bone Cements

Degradation of bone repairing composite of calcium polyphosphate fiber, calcium phospate cement and micromorselized bone in vitro

Structure and Properties of Bioactive Glass-Modified Calcium Phosphate/Calcium Sulfate Biphasic Porous Self-Curing Bone Repair Materials and Preliminary Research on Their Osteogenic Effect

The Influence of Sr and H3PO4 Concentration on the Hydration of SrCaHA Bone Cement.

Calcium Phosphate Coating on Magnesium Alloy for Modification of Degradation Behavior

In Vitro Degradability, Bioactivity And Primary Cell Responses To Bone Cements Containing Mesoporous Magnesium-Calcium Silicate And Calcium Sulfate For Bone Regeneration

Magnesium Phosphate/Polybutylene Succinate Composite for Bone Repair

Porous Mg–Zn–Ca scaffolds for bone repair: a study on microstructure, mechanical properties and in vitro degradation behavior