Abstract:Objective: One of the disadvantages of using CSC (calcium sulfate cement) in vivo is its weak osteogenic activity. Thus composite materials based on CSC have been recently studied. Silica-based mesoporous material (SBA-15) shows great potential for biological applications because of its functionalized surfaces and biocompatibility. We assumed that blending SBA-15 into CSC could improve the osteogenic activity of the CSC. Methods: SBA-15 was blended into CSC powder at a mass ratio of 5%, 10% and 20% to make a CSC/SBA composite. Four groups including CSC (pure CSC), CSC-5S (5% mass ratio), CSC-10S (10% mass ratio) and CSC-20S (20% mass ratio) group were designed. The cell adherence was assessed using the cell counting. The cell proliferation was determined by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. The osteogenic differentiation was evaluated using alkaline phosphatase (ALP) staining, alizarin red staining analysis, and the expression levels of osteogenic related genes, mainly ALP, collagen I (COL1), osteopontin and osteocalcin. An in vivo animal study was performed using the radius bone defect in a rabbit model. The micro computed tomography (CT) and histological evaluation were used to investigate bone formation. Results: The number of adhered cells on the CSC-10S and CSC-20S surface was higher than that on CSC and CSC-5S surface. The relative cell proliferation rate in CSC/SBA group was higher than that in CSC group. Compared with CSC and CSC-5S group, ALP staining in CSC-10S and CSC-20S group was increased. Alizarin red staining in the different CSC/SBA groups was higher than that in the CSC group. Higher expression levels of osteogenic differentiation-related genes were seen in cells grown on CSC/SBA composite. Micro CT and histological evaluation confirmed that CSC/SBA composite improved the efficiency of new bone formation in the bone defect. The above osteogenic activities were enhanced with increased mass ratio of SBS-15 in CSC/SBA composite. Conclusion: Incorporation of SBA-15 into CSC could greatly improve the osteogenic activity of CSC, implying the CSC/SBA composite are more beneficial to the bone repairing than pristine CSC.

Degradability and Osteogenesis of Mesoporous Magnesium Silicate Modified Calcium Sulphate Bone Cement

In Vitro Degradability, Bioactivity And Primary Cell Responses To Bone Cements Containing Mesoporous Magnesium-Calcium Silicate And Calcium Sulfate For Bone Regeneration

Influences of Doping Mesoporous Magnesium Silicate on Water Absorption, Drug Release, Degradability, Apatite-Mineralization and Primary Cells Responses to Calcium Sulfate Based Bone Cements.

Improvement of bioactivity, degradability, and cytocompatibility of biocement by addition of mesoporous magnesium silicate into sodium-magnesium phosphate cement

A Bioactive Degradable Composite Bone Cement Based on Calcium Sulfate and Magnesium Polyphosphate

Promotion of in Vivo Degradability, Vascularization and Osteogenesis of Calcium Sulfate-Based Bone Cements Containing Nanoporous Lithium Doping Magnesium Silicate

Study on Mesoporous Calcium Silicate/calcium Sulfate Bone Cement for Repair of Traumatic Bone Defect

Effects of Mesoporous Calcium Magnesium Silicate on Setting Time, Compressive Strength, Apatite Formation, Degradability and Cell Behavior to Magnesium Phosphate Based Bone Cements

Stimulatory effects of the fast setting and suitable degrading Ca-Si-Mg cement on both cementogenesis and angiogenesis differentiation of human periodontal ligament cells

Preparation of in situ forming and injectable alginate/mesoporous Sr-containing calcium silicate composite cement for bone repair

Effects of Magnesium Silicate on the Mechanical Properties, Biocompatibility, Bioactivity, Degradability, and Osteogenesis of Poly(butylene Succinate)-Based Composite Scaffolds for Bone Repair.

Novel, Degradable, and Cytoactive Bone Cements Based on Magnesium Polyphosphate and Calcium Citrate

Influence of Monocalcium Phosphate on the Properties of Bioactive Magnesium Phosphate Bone Cement for Bone Regeneration

A Composite of Cubic Calcium-Magnesium Sulfate and Bioglass for Bone Repair

A bioactive magnesium phosphate cement incorporating chondroitin sulfate for bone regeneration

Developing a Novel Magnesium Calcium Phosphate/sodium Alginate Composite Cement with High Strength and Proper Self-Setting Time for Bone Repair

Manipulation of the Degradation Behavior of Calcium Phosphate and Calcium Sulfate Bone Cement System by the Addition of Micro-Nano Calcium Phosphate

Difference of Osteoporotic Bone Fracture Healing Between Pure Magnesium and Magnesium Chloride (mgcl2) Enriched Calcium Sulphate/phosphate Cement (CSPC)

Bioactive calcium sulfate/magnesium phosphate cement for bone substitute applications

Calcium Sulfate Cement Combined With Silica-Based Mesoporous Material For Bone Regeneration: In Vitro And In Vivo Study

Multifunctional magnesium-organic framework doped biodegradable bone cement for antibacterial growth, inflammatory regulation and osteogenic differentiation