Abstract:Li-ion batteries are widely used in portable electronics and electric vehicles nowadays, since they have high energy densities and light-weighted designs. In pursuit of larger capacity, potential alloy materials such as Si, Sn, and Sb have been introduced as alternative anode materials to graphite. However, those electrodes experience irreversible mechanical degradation already after few charge/discharge cycles due to high stresses. Those stresses arise from changes in lattice dimensions and crystal structures, which are associated with overall volume changes and phase transformation. In this presentation, a Cahn–Hilliard-type diffusion model coupled with large strains is formulated [1, 2]. Thereby the electrochemical reaction is modeled through a modified Butler–Volmer equation to account for the influence of the phase change and mechanical stresses on the reaction fronts. Moreover, concentration-dependency of the elastic moduli and the anisotropy of the diffusivity are also covered. The 3D numerical simulations are carried out by isogeometric finite element methods in order to treat the high order differential equations in a straightforward sense. Illustrative simulation examples are demonstrated to reveal the electrochemical reactions on particle surfaces and phase interfaces. Results show that the ratio between the timescale of reaction and the diffusion can have a significant influence on phase segregation behavior, so does the anisotropy of diffusivity. In turn, the distribution of the lithium concentration greatly influences the reaction on the surface, especially when the phase interfaces appear on exterior surfaces. The reaction rate increases considerably at phase interfaces, due to the large lithium concentration gradient. In the next step, we introduce a fracture order parameter in the phasefield formulation to incorporate the crack in the particle [2, 3]. Simulation results demonstrate that the segregation of a Li-rich and a Li-poor phase during delithiation can drive the cracks to propagate. Acknowledgements. This work is supported by the “Excellence Initiative” of the German Federal and State Governments and the Graduate School of Computational Engineering at the Technische Universität Darmstadt. The author Xu would particularly like to thank the Adolf Messer Foundation for awarding her the Adolf Messer Price and for the financial support.

Debonding at the Interface Between Active Particles and PVDF Binder in Li-ion Batteries

(Invited) Understanding the Coupled Electrochemical-Mechanical Behavior of Materials for Improving the Performance and Durability of Lithium-Ion Batteries

Molecular Dynamics Simulations of the Traction-Separation Response at the Interface Between PVDF Binder and Graphite in the Electrode of Li-Ion Batteries

Molecular Dynamics Study of the Separation Behavior at the Interface between PVDF Binder and Copper Current Collector

A mathematical model for mechanically-induced deterioration of the binder in lithium-ion electrodes

A numerical study of mechanical degradation of Carbon-Coated Graphite Active Particles in Li-ion battery anodes

Numerical Analysis of Degradation and Capacity Loss in Graphite Active Particles of Li-Ion Battery Anodes

Modeling storage particle delamination and electrolyte cracking in cathodes of solid state batteries

Concentration Dependent Properties and Plastic Deformation Facilitate Instability of the Solid-Electrolyte Interphase in Li-ion Batteries

Mechanical Stability of the Heterogenous Bilayer Solid Electrolyte Interphase in the Electrodes of Lithium–Ion Batteries

Role of Polymeric Binders on Mechanical Behavior and Cracking Resistance of Silicon Composite Electrodes During Electrochemical Cycling

Capacity fading and inter/intra-granular fracture of polycrystalline cathode particle induced by charge/discharge cycles: A numerical study

A Three-Dimensional Electrochemical-Mechanical Model at the Particle Level for Lithium-Ion Battery

Micromechanisms of Capacity Fade in Silicon Anode for Lithium-Ion Batteries

Modelling the Morphological Background to Capacity Fade in Si-based Lithium-Ion Batteries

Influence of Mechanical Degradation in Polycrystalline NMC Particles on the Electrochemical Performance of Lithium-Ion Batteries

Impact of binder content on particle fracture and microstructure of solvent-free electrodes for Li-ion batteries

Multiscale Modeling of Electro-Chemo-Mechanical Degradation in Si/C Core–Shell Anode for the Lithium-Ion Battery of High Energy Density

Electro-chemo-mechanical behavior of lithium-ion battery electrodes

Deformation and Failure of Lithium-Ion Batteries Treated As a Discrete Layered Structure

SEI-Coated Carbon Particles: Electrochemomechanical Fracture Mechanisms