Abstract:Luminescent pyrene-functionalized nano-SiO2 (nano-SiO(2)Pyr) hybrids were synthesized and characterized using thermogravimetry, infrared, UV-vis absorption and, X-ray photoelectron spectroscopy, as well as field emission transmission electron microscopy (FETEM). The organic substituents immobilized on the nano-SiO(2)Pyr hybrids accounted for approximately 10% of the total weight. Polyethylene glycol 200 (PEG200) was found to be the most suitable solvent to suspend the nano-SiO(2)Pyr hybrids compared to other commonly used organic solvents. FETEM images indicated an average SiO2 nanoparticle diameter of approximately 12 nm and a 1- to 2-nm thick organic species functionalization layer. Several emission peaks were recorded at wavelengths of 380-580 nm and were designated as emissions arising from either the monomer or excimer of the pyrene substituents. Excimer formation was concentration and solvent polarity dependent, with higher concentrations and a stronger solvent polarity benefiting excimer formation. Further, nano-SiO(2)Pyr hybrids were doped in poly(methyl naethacrylate) (PMMA) thin films; fluorescence spectra indicated that the excimer could be formed almost exclusively from neighboring nano-SiO(2)Pyr hybrids. Time-resolved fluorescence decays revealed that the emission lifetimes of nano-SiO(2)Pyr monomers and excimers were approximately 190 ns and 65-100 ns in the PEG200 solution, respectively, which was shortened to 0.45 ns to tens of ns in doped PMMA thin films, depending on the nano-hybrid concentration. Thus, the present study not only provides a method to prepare luminescent nano-materials but also a route to investigate excimer formation in solutions and thin films. (C) 2016 Elsevier B.V. All rights reserved.

Photoluminescent epoxy microspheres: preparation, surface functionalization via grafting polymerization and photophysical properties

Nanostructured Epoxy Thermosets Containing Poly(Vinylidene Fluoride): Preparation, Morphologies, and Dielectric Properties

Luminescent and light refractive polymers: Synthesis and optical and photonic properties of poly(arylene ethynylene)s carrying silole and tetraphenylethene luminogenic units

Development of Structure-tailored and Composite Magnetic-Fluorescent Microspheres Through the PRI Method

Photoluminescent nanoparticles in water with tunable emission for coating and ink-jet printing

Crosslinked Epoxy Microspheres: Preparation, Surface-Initiated Polymerization, And Use As Macroporous Silica Porogen

White Light Emission of Multi-Chromophore Photoluminescent Nanoparticles Using Polyacrylate Scaffold Copolymers with Pendent Polyfluorene Groups

Photophysical and dielectric properties of nanostructured epoxy thermosets containing poly(N-vinylcarbazole) nanophases

Synthesis and photoluminescence modulating of polypyrrole fluorescent nano-spheres/dots

Preparation of mono-dispersed fluorescent PMMA/GMA/DVB polymer microspheres with different sizes

Fabrication and Functionalization of Dendritic Poly(Amidoamine)-Immobilized Magnetic Polymer Composite Microspheres

Photoactivation‐Induced Emission Enhancement in Benzosilole‐Based Fluorescent Conjugated Microporous Polymer Microspheres with Converse‐Photobleaching Behavior

Synthesis and Applications of Water‐dispersible Microspheres Containing Arborescent PAMAM Surfaces

Preparation of Uniform Rhodamine B-doped Poly(3-Glycidoxypropylsilsesquioxane) Fluorescent Microspheres Via a Sol–gel Method

Preparation of CdTe-loaded crosslinked polystyrene fluorescent microspheres by miniemulsion polymerization

Incorporating fluorescent dyes into monodisperse melamine–formaldehyde resin microspheres via an organic sol–gel process: a pre-polymer doping strategy

Photoluminescent polymeric micelles from poly(ethylene oxide)-block-poly(((4-vinylphenyl)ethene-1,1,2-triyl)tribenzene) diblock copolymers

Preparation of Monodisperse, Superparamagnetic, Luminescent, and Multifunctional PGMA Microspheres with Amino-Groups

Synthesis and Photophysical Properties of Pyrene-Functionalized Nano-Sio2 Hybrids in Solutions and Doped-Pmma Thin Films

Preparation of polypropylene nanofibers reinforced multifunctional epoxy composite concrete with ultraviolet‐driven afterglow emission

Fabrication, Morphologies and Properties of Luminescent PMMA Porous Nano-Fibers