Abstract:A multilayer CrSi2/MoSi2/SiC–Mo2C composite anti-oxidation coating was in-situ prepared on Mo substrate by a three-step pack cementation method. Energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) tests indicated that the coating was composed of CrSi2, MoSi2, SiC and Mo2C. Furthermore, back scattered electron (BSE) and electron probe microanalysis (EPMA) analyses demonstrated that the whole composite coating was about 65μm and the outermost layer was a composite which was composed of CrSi2, MoSi2 and SiC, and just beneath it was a Mo2C transitional layer which connected the outer layer and the substrate Mo. Since the distribution of the elements in the composite coating was gradually increased or decreased and thus no distinguished interface arose during the preparation process. Cyclic oxidation experiments indicated that the mass loss was only 5.01wt.% in 120min at 1600°C for CrSi2/MoSi2/SiC–Mo2C coated samples, which was much lower than that of MoSi2/SiC–Mo2C coated ones. Besides the Si diffusion hindrance effects of Mo2C transitional layer, BSE, surface profilometer and EPMA observations proved that Cr in the form of CrSi2 could not only reduce the mismatch between the coating and the substrate through the formation of Cr2O3, but also accelerate the formation of a mixed protecting oxide scale at low temperature. Moreover, the Cr2O3 in the scale might also stabilize the glassy coating at high temperature by restraining the volatilization of SiO2.

Fabricate of Mo-Si-N anti-oxidation coating for C/C composites

Mo-Si-C-N Multi-Layer Anti-Oxidation Coating on C/C Composites

Optimum Compositions of Si3N4 -Mosi2/si- SiC Anti-Oxidation Coating for C/C Composites

Microstructure of A Mo-Si-C-N Multi-Layered Anti-Oxidation Coating on Carbon/Carbon Composites by Fused Slurry

Formation and Oxidation Behavior of Mo-Si-B Composite Coatings with B-rich Interlayer Prepared by Slurry Sintering Method

Microstructure Characterization of Mo–Si–C–N Anti-Oxidation Coatings on C/C Composites

Effect of heat-treatment on the oxidation resistance of Mo-Si-N coating for C/C composites

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process

Phase Constitutions of MoSiN Anti-Oxidation Multi-Layer Coatings on CC Composites by Fused Slurry

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

Microstructure and Oxidation Resistant Property of C/C Composites Modified by SiC–MoSi2–CrSi2 Coating

In-situ fabrication of MoSi 2 /SiC–Mo 2 C gradient anti-oxidation coating on Mo substrate and the crucial effect of Mo 2 C barrier layer at high temperature

Fabrication of CrSi2/MoSi2/SiC–Mo2C Gradient Composite Coating on Mo Substrate and the Stabilizing Effect of Cr on the Coating's Anti-Oxidation Properties

Effect of Mo/Si Ratio on the Microstructure and Oxidation Resistance of Si-Mo Coating for C/C Composites

SiCn/SiC Oxidation Protective Coating for Carbon/carbon Composites

SiC Nanowire-Toughened SiC–MoSi2–CrSi2 Oxidation Protective Coating for Carbon/carbon Composites

Effect of Al content in an Al/Si layer on the oxidation behavior of the Mo/Si-Al/Si double-layer coated C/C composites at 1370°C

Oxidation Protection of C/C Composites by Ultra Long SiC Nanowire-Reinforced SiC–Si Coating

Effect of Al Content in an Al/Si Layer on the Oxidation Behavior of the Mo/Si–Al/Si Double-Layer Coated C/C Composites at 1370 °C

Oxidation Protection of C/C Composites with a Multilayer Coating of SiC and Si + SiC + SiC Nanowires

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites