Abstract:Ytterbium-sensitized erbium-doped oxide-halide tellurite and germanate-niobic-lead glasses have been synthesized by conventional melting method. Intense green and red emissions centered at 525, 546 and 657 nm, corresponding to the transitions 2H11/2-->4I15/2, 4S3/2-->4I15/2 and 4F9/2-->4I15/2, respectively, were simultaneously observed at room temperature in these glasses. The quadratic dependence of the 525, 546 and 657 nm emissions on excitation power indicates that a two-photon absorption process occurs. Tellurite glass showed a weaker up-conversion emission than germanate-niobic-lead glass, which is inconsistent with the prediction from the difference of maximum phonon energy between tellurite and germanate-niobic-lead glasses. In this paper, Raman spectroscopy was employed to investigate the origin of the difference in up-conversion luminescence in the two glasses. Compared with phonon side-band spectroscopy, Raman spectroscopy extracts more information including both phonon energy and phonon density. Our results reveal that the phonon density and the maximum phonon energy of host glasses are both important factors in determining the up-conversion efficiency.

Strong Upconversion Luminescence in Er3+/Yb3+-doped Halide Modified Tellurite Glass

High Efficiency Infrared to Visible Upconversion in Er3+/Yb3+-Doped Lead Halide Tellurite Glass

Optical Transitions And Upconversion Luminescence Of Er3+/Yb3+-Codoped Halide Modified Tellurite Glasses

Upconversion Luminescence Property of Er3+ and Yb3+ Co-doped Germanium Silicate Glass

Upconversion emissions in Yb 3+ –Tm 3+ -doped tellurite glasses excited at 976 nm

Up-Conversion Luminescence Analysis in Ytterbium-Sensitized Erbium-Doped Oxide-Halide Tellurite and Germanate-Niobic-Lead Glasses

Upconversion emissions in Yb<sup>3+</sup>–Tm<sup>3+</sup>-doped tellurite glasses excited at 976 nm

Preparation and Properties of Rare Earth Doped Glass Ceramics with Upconversion Luminescence Behaviors

Energy transfer and infrared-to-visible upconversion luminescence of Er3+/Yb3+-codoped halide modified tellurite glasses

Upconversion luminescence of Er3+-doped oxyfluoride tellurite glass

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Upconversion Luminescence of Yb3+/Tb3+/Er3+-Doped Fluorosilicate Glass Ceramics Containing Srf2 Nanocrystals

Blue Upconversion Luminescence in Tm3+/Yb3+-Codoped Lead Chloride Tellurite Glass

Enhancement of upconversion luminescence in Er3+ doped tellurite glasses due to the introduction of PbCl2

The Luminescence of Er3+,Yb3+,Tm3+-codoped Tellurite Glass Pumped at 970Nm

Upconversion fluorescence spectroscopy of Er3+/Yb3+-codoped lead oxyfluorosilicate glass

Intense Upconversion Luminescence of Er3+/Yb3+ Codoped Oxyfluoride Borosilicate Glass Ceramics Containing Ba2GdF7 Nanocrystals

Up-conversion luminescence and near infrared luminescence of Er3+ in transparent oxyfluoride glass-ceramics

Effect of Yb3+concentration on Upconversion Emission of Er3+-doped Tellurite Glass

Composition dependent frequency upconversion of Er3+/Yb 3+-codoped lead chloride tellurite glasses

Upconversion emissions in Yb–Tm-doped tellurite glasses excited at 976 nm