Abstract:We have developed a new porous metal-organic framework (MOF) (UTSA-80) with an elongated anthracene derivative as a linker. The activated UTSA-80a has a pore volume of 1.03 cm(3) g(-1) and a gravimetric Brunauer-Emmett-Teller surface area of ca. 2280 m(2) g(-1), higher than those of PCN-14. The volumetric methane storage capacity of UTSA-80a at 35 bar and 298 K is 192 cm(3) (STP) cm(-3), which makes it one of the few porous MOFs with a storage capacity > 190 cm(3) (STP) cm(-3) at 35 bar. The volumetric uptake of methane by UTSA-80a reaches 233 cm(3) (STP) cm(-3) at room temperature and 65 bar; this is 88.6% of the new volumetric target of the US Department of Energy if the packing density loss is ignored. This capacity is comparable with that of PCN-14. However, as a result of the lower methane uptake of UTSA-80a at 5 bar, it has a much higher methane storage working capacity (deliverable amount of methane between 65 and 5 bar) of 174 cm(3) (STP) cm(-3) compared with PCN-14 [157-160 cm(3) (STP) cm(-3)]. This value is slightly lower than the 190 cm(3) (STP) cm(-3) achieved by HKUST-1, suggesting that it is a promising material for methane storage in transport applications. Such an exceptionally high working capacity can probably be attributed to the elongated anthracene derivative used as a linker within UTSA-80a, which adjusts the pore sizes/cages and interactions with the methane molecules to optimize the methane working capacity.

A new NbO type metal–organic framework for high acetylene and methane storage

A NbO type microporous metal–organic framework constructed from a naphthalene derived ligand for CH4 and C2H2 storage at room temperature

A Novel Metal-Organic Framework for High Storage and Separation of Acetylene at Room Temperature

Novel Microporous Metal-Organic Framework Exhibiting High Acetylene And Methane Storage Capacities

A Microporous Metal-Organic Framework with Polarized Trifluoromethyl Groups for High Methane Storage.

A novel methoxy-decorated metal–organic framework exhibiting high acetylene and carbon dioxide storage capacities

An amino-decorated NbO-type metal–organic framework for high C2H2 storage and selective CO2 capture

A Highly Porous Nbo Type Metal-Organic Framework Constructed from an Expanded Tetracarboxylate

A microporous metal-organic framework with both open metal and Lewis basic pyridyl sites for high C2H2 and CH4 storage at room temperature.

A Robust Microporous Metal–organic Framework Constructed from a Flexible Organic Linker for Acetylene Storage at Ambient Temperature

A Novel NbO-type Metal-Organic Framework for Highly Separation of Methane from C2-hydrocarbon at Room Temperature

A Fluorinated Metal–Organic Framework for High Methane Storage at Room Temperature

A new anionic metal–organic framework showing tunable emission by lanthanide(III) doping and highly selective CO2 adsorption properties

A New Metal–organic Framework with Potential for Adsorptive Separation of Methane from Carbon Dioxide, Acetylene, Ethylene, and Ethane Established by Simulated Breakthrough Experiments

A Porous Metal–organic Framework with an Elongated Anthracene Derivative Exhibiting a High Working Capacity for the Storage of Methane

A New Microporous Metal–organic Framework with Potential for Highly Selective Separation Methane from Acetylene, Ethylene and Ethane at Room Temperature

A New Mfj-Type Metal–organic Framework Constructed from a Methoxyl Derived V-shaped Ligand and Its H2, CO2 and CH4 Adsorption Properties

High Gas adsorption Capacity of an agw-type Metal-organic Framework Decorated with Methyl Groups

Microporous metal-organic frameworks with suitable pore spaces for acetylene storage and purification

A Metal–Organic Framework with Optimized Porosity and Functional Sites for High Gravimetric and Volumetric Methane Storage Working Capacities

A Fluorinated Zr-based MOF of High Porosity for High CH4 Storage