Microstructure evolution of hot-deformed powder metallurgy Ti-45Al-7Nb-0.3W alloy during heat treatment

ZHAO Kun,LIU Yong,HUANG Lan,LIU Bin,LI Jian-bo,LIANG Xiao-peng,HE Yue-hui
2014-01-01
The Chinese Journal of Nonferrous Metals
Abstract:Powder metallurgy Ti-45Al-7Nb-0.3W (mole fraction, %) alloy was canned-forged and then heat-treated. The effects of heat treatment time and temperature on the alloy microstructure evolution were studied. The microstructures of as-forged alloy and heat-treated alloy were investigated by scanning and transmission microscopy. The results demonstrate that a fewβ grains in as-forged alloy are eliminated during heat treatments in the temperature range of 1230?1260℃. Isochronal annealing experiments show that theα grain size andγ grain size rapidly increase with increasing the temperature, while the volume fraction ofγ phase steeply decreases andα grains become equiaxial. Isothermal annealing experiments at 1260℃ for 0.5?6 h reveal a sharp increase ofα grain size andγ grain size with time. Meantime, the volume fraction ofγ phase decreases. The microstructure of alloy shows no significant change during prolonging the annealing time. By calculation, the extremeα grain size at 1260℃ is approximately 0.54Dγ/Vγ (Dγ is short forγ grain size andVγ is short or the volume fraction ofγ phase).
What problem does this paper attempt to address?