Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

In Situ DRIFTS Study of the Low Temperature Selective Catalytic Reduction of NO with NH3 over MnOx Supported on Multi-Walled Carbon Nanotubes Catalysts

In Situ Drifts Studies on Mnox Nanowires Supported by Activated Semi-Coke for Low Temperature Selective Catalytic Reduction of Nox with Nh3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

In Situ FT-IR Study of Highly Dispersed MnO X /SAPO-34 Catalyst for Low-Temperature Selective Catalytic Reduction of NO X by NH 3

In Situ DRIFTS Study of the Mechanism of Low Temperature Selective Catalytic Reduction over Manganese-Iron Oxides

DRIFT Study of Manganese/Titania-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO with NH<sub>3</sub>

In situ FT-IR studies on low temperature NH3-SCR mechanism of NOx over MnOx/WO3/TiO2catalyst

Manganese Oxides Supported on Multi-Walled Carbon Nanotubes for Selective Catalytic Reduction of NO with NH3: Catalytic Activity and Characterization

The Role of NH_3 in the Low-Temperature Selective Catalytic Reduction of NO over MnO_x/TiO_2

Low-temperature Selective Catalytic Reduction of NO with NH3 over Nanoflaky MnOx on Carbon Nanotubes in Situ Prepared Via a Chemical Bath Deposition Route

The role of NH3 in the low-temperature selective catalytic reduction of NO over MnOx/TiO2

In Situ DRIFTS Investigation on the SCR of NO with NH3 over V2O5 Catalyst Supported by Activated Semi-Coke

Mechanism Study of FeW Mixed Oxides to the Selective Catalytic Reduction of NOx with NH3: in Situ DRIFTS and MS

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Molecular-Level Insight into Selective Catalytic Reduction of NOx with NH3 to N2 over a Highly Efficient Bifunctional Va-MnOx Catalyst at Low Temperature

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Insight into the Dynamic Behaviors of Reactants with Temperature over a TiOx-based Catalyst for NOx Removal Via NH3-SCR

Highly dispersed MnOx-FeO(x)supported by silicalite-1 for the selective catalytic reduction of NO(x)with NH(3)at low temperatures

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

Insights into the selective catalytic reduction of NO by NH 3 over Mn 3 O 4 (110): a DFT study coupled with microkinetic analysis

Study on the Role of Mn Species in Low Temperature SCR on MnOx/TiO2 Through Experiment and DFT Calculation