Dual Yolk-Shell Structure of Carbon and Silica-Coated Silicon for High-Performance Lithium-Ion Batteries

L. Y. Yang,H. Z. Li,J. Liu,Z. Q. Sun,S. S. Tang,M. Lei

DOI: https://doi.org/10.1038/srep10908

IF: 4.6

2015-01-01

Scientific Reports

Abstract:Silicon batteries have attracted much attention in recent years due to their high theoretical capacity, although a rapid capacity fade is normally observed, attributed mainly to volume expansion during lithiation. Here, we report for the first time successful synthesis of Si/void/SiO 2 /void/C nanostructures. The synthesis strategy only involves selective etching of SiO 2 in Si/SiO 2 /C structures with hydrofluoric acid solution. Compared with reported results, such novel structures include a hard SiO 2 -coated layer, a conductive carbon-coated layer and two internal void spaces. In the structures, the carbon can enhance conductivity, the SiO 2 layer has mechanically strong qualities and the two internal void spaces can confine and accommodate volume expansion of silicon during lithiation. Therefore, these specially designed dual yolk-shell structures exhibit a stable and high capacity of 956 mA h g −1 after 430 cycles with capacity retention of 83%, while the capacity of Si/C core-shell structures rapidly decreases in the first ten cycles under the same experimental conditions. The novel dual yolk-shell structures developed for Si can also be extended to other battery materials that undergo large volume changes.