Dual carbon and void space confined SiOx/C@void@Si/C yolk-shell nanospheres with high-rate performances and outstanding cyclability for lithium-ion batteries anodes

Wenyan Chen,Shaojie Kuang,Hongshan Wei,Peizhen Wu,Tang Tang,Hailin Li,Yeru Liang,Xiaoyuan Yu,Jingfang Yu

DOI: https://doi.org/10.1016/j.jcis.2021.11.099

IF: 9.9

2022-03-01

Journal of Colloid and Interface Science

Abstract:Silicon-based anode materials with high theoretical capacity have great challenges of enormous volume expansion and poor electronic conductivity. Herein, a novel dual carbon confined SiO_x/C@void@Si/C yolk-shell monodisperse nanosphere with void space have been fabricated through hydrothermal reaction, carbonization, and in-situ low-temperature aluminothermic reduction. Furthermore, the O/Si ratio and void space between SiO_x/C core and Si/C shell can be effectively tuned by the length of aluminothermic reduction time. The SiO_x/C core plays a role of maintaining the spherical structure and the void space can accommodate the volume expansion of Si. Moreover, the inner and outer carbons not only alleviate volume variation of SiO_x and Si but also enhance the electrical conductivity of composites. Benefiting from the synergy of the double carbon and void space, the optimized VSC-14 anode affords prominent cycle stability with reversible capacity of 1094 mAh g^-1 after 550 cycles at 200 mA g^-1. By pre-lithiation treatment, the VSC-14 achieves an initial Coulombic efficiency of 93.27% at 200 mA g^-1 and a reversible capacity of 348 mAh g^-1 at 5 A g^-1 after 4000 cycles. Furthermore, the pouch cell using VSC-14 anode and LiFePO₄ cathode delivers a reversible capacity of 138 mAh g^-1 at 0.2C. We hope this strategy can provide a scientific method to synthesis yolk-shell Si-based materials.

chemistry, physical