Abstract:In this study, ionic liquids and carbon nanotubes were used to prepare PEI composite fibers (PEI/CNT‐IL) successfully. When the contents of CNT and IL are 0.5% and 1.0%, respectively, PEI/CNT‐IL composite fiber can realize the optimal performance. PEI/0.5%CNT‐1.0%IL composite fiber achieves the breaking stress of 2.0 cN/dtex, and the electrical conductivity of 1.06×10‐5 S/cm without any negative influence on the heat resistance. Polyetherimide (PEI) has been widely applied in the form of plastics, films, and foam materials. But PEI fiber is confronted with some challenges, such as high melt viscosity and high spinning temperature during the spinning process, poor mechanical properties because of its amorphous structure. In this study, ionic liquids (ILs) and carbon nanotubes (CNTs) were used to prepare PEI composite fibers (PEI/CNT‐IL) successfully, which were further characterized by scanning electron microscope (SEM), Raman spectra, differential scanning calorimetry, dynamic mechanical analysis, thermalgravimetric analysis, mechanical property, and conductivity measurements. IL showed a plasticizing effect to reduce the processing temperature of PEI and SEM images showed that CNTs were uniformly dispersed in the PEI matrix by the assistance of IL. The synergistic effect of CNT and IL thus improved the tensile strength and antistatic properties of PEI fibers. When the contents of CNT and IL were 0.5 and 1.0 wt%, respectively, the optimal properties were obtained. PEI/CNT‐IL fibers exhibited a maximum tensile strength of 2.0 cN/dtex with the elongation at break being 90%, and the enhanced electrical conductivity of 10−5 S·cm−1, which was increased by 13 orders of magnitude compared to that of pristine PEI fiber. Highlights PEI composite fibers were prepared via melt spinning with the assistance of IL and CNT. IL can effectively disperse CNT and plasticize PEI to reduce the processing temperature. The synergistic effect of CNT and IL has improved the tensile strength and antistatic properties of PEI fibers.

Fabrication and application of silicalite-1 and TS-1 hollow fibers with polyethylene imine (PEI) fibers as substrates

Fabrication and characterization of porous tubular silk fibroin scaffolds.

Fabrication of Homogeneous Mullite-Based Fiber Porous Ceramics with High Strength and Porosity

Controlled Release of Siliceous Species for the Fabrication of Highly B-Oriented MFI Zeolite Films

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Fabrication of hollow zeotite fibers by electrophoretic assembly of nanosilicalite-1

High performance zeolite NaA membranes synthesized on the inner surface of zeolite/PES–PI blend composite hollow fibers

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Thermal processing of zeolite seed layers for the fabrication of compact oriented MFI zeolite films

Solvent Resistant Self-Crosslinked Poly(ether Imide)

Fabrication of ZIF-8 Membranes on Dual-Layer ZnO-PES/PES Organic Hollow Fibers by In-Situ Crystallization

Preparation and properties of polyetherimide fibers based on the synergistic effect of carbon nanotubes and ionic liquids

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Fabrication and characterization of zein-based nanofibrous scaffolds by an electrospinning method.

Layer-by-layer assembly of nanozeolite - Zeolite coated fibers and hollow zeolite fibers

Effects of porogen EDTA on morphology of porous silica support and preparation of MFI zeolite membrane

Porous polyetherimide fiber fabricated by a facile micro-extrusion foaming for high temperature thermal insulation

Fabrication of Polyethyleneimine and Poly(styrene-<I>alt</I>-maleic Anhydride) Nanotubes Through Covalent Bond

Fabrication of Hollow Zeolite Fibers Through Layer-by-Layer Adsorption Method

Electrophoretic Assembly of Nanozeolites: Zeolite Coated Fibers and Hollow Zeolite Fibers

In Situ Preparation of Pei/Sio2 Composites and Their Modification for Epoxy Resin