Interface Stress Development in the Cu/Ag Nanostructured Multilayered Film During the Tensile Deformation

R. Su,L. Li,Z. H. Nie,Q. H. Zhang,Y. D. Wang,X. T. Zhou,Y. D. Wu,X. D. Hui,X. J. Li,M. G. Wang
DOI: https://doi.org/10.1063/1.4903342
IF: 4
2014-01-01
Applied Physics Letters
Abstract:Cu/Ag nanostructured multilayered films (NMFs) with different stacking sequences were investigated by synchrotron X-ray diffraction during the tensile deformations for interface stress study. The lattice strains were carefully traced and the stress partition, which usually occurs in the multiphase bulk metallic materials during plastic deformations, was first quantitatively analyzed in the NMFs here. The interface stress of the Cu/Ag NMFs was carefully analyzed during the tensile deformation and the results revealed that the interface stress was along the loading direction and exhibited three-stage evolution. This tensile interface stress has a detrimental effect on the deformation, leading to the early fracture of the NMFs.
What problem does this paper attempt to address?