Abstract:We present the fabrication of conductive graphitic microelectrodes in diamond by using pulsed Bessel beams in the burst mode laser writing regime. The graphitic wires are created in the bulk of a 500 {\mu}m thick monocrystalline HPHT diamond (with (100) orientation) perpendicular to the sample surface, without beam scanning or sample translation. In particular, the role of different burst features in the resistivity of such electrodes is investigated for two very different sub-pulse durations namely 200 fs and 10 ps, together with the role of thermal annealing. Micro-Raman spectroscopy is implemented to investigate the laser-induced crystalline modification, and the results obtained by using two different laser repetition rates, namely 20 Hz and 200 kHz, are compared. A comparison of the micro-Raman spectra and of the resistivity of the electrodes fabricated respectively with 10 ps single pulses and with bursts (of sub-pulses) of similar total duration has also been made, and we show that the burst mode writing regime allows to fabricate more conductive micro electrodes, thanks to the heat accumulation process leading to stronger graphitization. Moreover, the microfabrication of diamond by means of the longest available bursts (~ 46.7 ps duration) featured by 32 sub-pulses of 200 fs duration, with intra-burst time delay of 1.5 ps (sub-THz bursts), leads to graphitic wires with the lowest resistivity values obtained in this work, especially at low repetition rate such as 20 Hz. Indeed, micro electrodes with resistivity on the order of 0.01 {\Omega} cm can be fabricated by Bessel beams in the burst mode regime even when the bursts are constituted by femtosecond laser sub-pulses, in contrast with the results of the standard writing regime with single fs pulses typically leading to less conductive micro electrodes.

High Conductivity Micro-Wires In Diamond Following Arbitrary Paths

Thermal Conductivity of A New Carbon Nanotube Analog: the Diamond Nanothread

Submicron and Nano-Diameter Silica Wires for Optical Wave Guiding

Nanowiring Light

Directionality in Laser Fabrication of 3D Graphitic Microwires in Diamond

In Situ Fabrication and Graphitization of Amorphous Carbon Nanowires and Their Electrical Properties

Effect of Crystallographic Orientation on the Potential Barrier and Conductivity of Bessel Written Graphitic Electrodes in Diamond

Highly Conductive Paths in Diamond and their Application in High Pressure Measurements

Bessel beam fabrication of graphitic micro electrodes in diamond using laser bursts

Fabrication and electrical characterization of three-dimensional graphitic microchannels in single crystal diamond

Fabrication of crystalline submicro-to-nano carbon wire for achieving high current density and ultrastable current

Enhanced Tensile Ductility of Tungsten Microwires Via High-Density Dislocations and Reduced Grain Boundaries

Parallel laser fabrication of electrically conductive graphitic columns in diamond

Optimizing magnetoimpedance of amorphous microwires by nanocarbon-induced magnetic anisotropy

Ultrastrong conductive in situ composite composed of nanodiamond incoherently embedded in disordered multilayer graphene

Direct fabrication of three-dimensional buried conductive channels in single crystal diamond with ion microbeam induced graphitization

Abnormally High Thermal Conductivity in Fivefold Twinned Diamond Nanowires

Fabrication of Diamond Nanowires for Quantum Information Processing Applications

Fabrication of highly conductive carbon nanotube fibers for electrical application

Synthesis of Nano-Scale Silicon Wires by Excimer Laser Ablation at High Temperature

Electron Transport Properties of Atomic Carbon Nanowires between Graphene Electrodes