Abstract:This article reports on the fabrication of hybrid silica nanoparticles densely grafted with thermoresponsive poly(N-isopropylacrylamide) (PNIPAM) brushes and their thermal phase transition behavior. Surface-initiated atom transfer radical polymerization (ATRP) of N-isopropylacrylamide (NIPAM) was conducted in 2-propanol at ambient temperature using CuCl/CUCl2/tris(2-(dimethylamino)ethyl)amine (Me6TREN) as the catalytic system, starting from the surface of silica nanoparticles derivatized with ATRP initiators (0.35 nm(2)/initiator). The surface-initiated ATRP can be conducted in a well-controlled manner, as revealed by the linear kinetic plot, linear evolution of number-average molecular weights (M-n) versus monomer conversions, and the relatively narrow molecular weight distributions (M-w/M-n < 1.25) of the grafted PNIPAM chains. The grafting density of PNIPAM chains, at the surface of silica nanoparticls was estimated to be 2.2 nm(2)/chain based on transmission electron microscopy (TEM) and thermogravimetric analysis (TGA) characterization results. Laser light scattering (LLS) and optical transmittance were then employed to study the thermal phase transitions of PNIPAM brushes at the surface of silica nanoparticles. Both the intensity-average hydrodynamic radius, < R-h >, and average radius of gyration, < R-h >, exhibit a two-stage decrease upon heating over the broad temperature range of 20-37 degrees C, which is in contrast to the fact that free PNIPAM homopolymer in aqueous solution exhibits a phase transition at ca. 32 degrees C within a narrow temperature range. The first phase transition takes place in the temperature range of 20-30 degrees C, which can be tentatively ascribed to the n-cluster-induced collapse of the inner region of PNIPAM brushes close to the silica core; the second phase transition occurs above 30 degrees C, which can be ascribed to the outer region of PNIPAM brushes, possessing much lower chain density compared to that of the inner part. We tentatively expect that the observed unique double phase transition behavior of polymer brushes coated at the surface of inorganic nanoparticle cores can be further utilized to fabricate novel narrostructured devices with more complex functions.

Surfactant Free Fabrication of Polyimide Nanoparticles

Synthesis of poly(propylene glycol)-grafted polyimide precursors and preparation of nanoporous polyimides

Fabrication of non-collapsed hollow polymeric nanoparticles with shell thickness in the order of ten nanometres and anti-reflection coatings

Formation of Novel Polymeric Nanoparticles.

Studies on Novel Surfactant-Free Polystyrene Nanoparticles Formed in Microphase Inversion

Formation, Stabilization & Application of Polymeric Nanoparticles

Fabrication of nanoparticle array membranes by integrating semi-crystalline polymer self-assembly with NIPS for water treatment

Formation of Novel Polymeric

Modified Nanoprecipitation Method for Polysulfone Nanoparticles Preparation

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Surfactant-Free Preparation of Conjugated Polymer Nanoparticles in Aqueous Dispersions Using Sulfate Functionalized Fluorene Monomers

Controllable Fabrication of Highly Uniform Sub‐10 nm Nanoparticles from Spontaneous Confined Nanoemulsification (Small 34/2023)

Fabrication of nickel oxide nanocomposite layer on a flexible polyimide substrate via ion exchange technique

Preparation of Polyetherimide Nanoparticles by a Droplet Evaporation-Assisted Thermally Induced Phase-Separation Method

Fabrication of Hybrid Silica Nanoparticles Densely Grafted with Thermoresponsive Poly(N-isopropylacrylamide) Brushes of Controlled Thickness Via Surface-Initiated Atom Transfer Radical Polymerization

On-water surface synthesis of crystalline, few-layer two-dimensional polymers assisted by surfactant monolayers

Fabrication of Surfaces with Nanoislands of Chemical Functionality by the Phase Separation of Self-Assembling Monolayers on Silicon

Polymeric Microparticles Generated via Confinement‐Free Fluid Instability

Preparation of Nanoporous Polyimide Thin Films Via Layer-By-Layer Self-Assembly of Cowpea Mosaic Virus and Poly(Amic Acid)

Polyamide nanofiltration membranes by vacuum-assisted interfacial polymerization: Broad universality of Substrate, wide window of monomer concentration and high reproducibility of performance

Reactive Nanoparticles Compatibilized Immiscible Polymer Blends: Synthesis of Reactive SiO2 with Long Poly(methyl methacrylate) Chains and the in Situ Formation of Janus SiO2 Nanoparticles Anchored Exclusively at the Interface.