Abstract:Ba1-xKxFe2As2 superconductors have strong potential for magnet applications through their very high upper critical field, relatively high superconducting transition temperature and manufacturability through the powder-in-tube (PIT) route. However, the critical current density in PIT tapes is still low compared to the incumbent technologies, so a greater understanding of the limiting factors is required. We have measured in-field critical currents (Ic) of stainless steel and silver double-sheathed monofilament Ba0.6K0.4Fe2As2 superconductor tapes at elevated temperatures from 15 K to 35 K. At 20 K the critical current density is up to 140 kA/cm2 in low (optimal) field and 22 kA/cm2 in 8 T. In the low-field region we observe an anomalous and sharp suppression of Ic centred at zero field. This feature is non-hysteretic for lower temperatures and perpendicular field, but becomes hysteretic for higher temperatures in perpendicular field and all temperatures in parallel field. The low-field suppression is reflected also in the n-values which can otherwise be very high, in excess of 100, in optimal field. Magnetic-field hysteresis of Ic is generally attributed to flux exclusion / flux trapping in granular superconductors and this is likely to be the case also in the present conductors. The low-field Ic anomaly also likely has its origin in the planar granularity, while magnetic phases in grains or grain boundaries may also play a role.

Direct Observation Of The Depairing Current Density In Single-Crystalline Ba0.5k0.5fe2as2 Microbridge With Nanoscale Thickness

Depairing Current Density of Ba0.5K0.5Fe1.95Co0.05As2 Microbridges with Nanoscale Thickness

Normal-state resistivity and the depairing current density of BaFe$_2$(As,P)$_2$ nanobridges along the $c$ axis

High, Magnetic Field Independent Critical Currents In (Ba,K)Fe2as2 Crystals

Vortex Creep and Critical Current Densities in Superconducting (ba,k)fe2as2 Single Crystals

Evidence for Multi-Gap Symmetry from Grain Boundary Effects in Polycrystalline Ba0.6k0.4fe2as2 Microbridge

Intrinsic Superconducting Transport Properties of Ultra-Thin Fe1+y Te0.6Se0.4 Microbridges

Low field anomaly in the critical current of Ba1‐xKxFe2As2 tapes

Anisotropic physical properties and large critical current density in KCa${_2}$Fe${_4}$As${_4}$F${_2}$ single crystal

Evidence for Two Energy Gaps in Superconducting Ba0.6k0.4fe2as2 Single Crystals and the Breakdown of the Uemura Plot

Upper Critical Fields and Anisotropy of BaFe 1.9 Ni 0.1 As 2 Single Crystals

Dissipation in an Ultrathin Superconducting Single-Crystal Pb Nanobridge

Transport Properties, Upper Critical Field and Anisotropy of Ba(Fe0.75Ru0.25)2As2 Single Crystals

Upper Critical Field, Anisotropy, And Superconducting Properties Of Ba1-Xkxfe2as2 Single Crystals

Approaching the ultimate superconducting properties of (Ba,K)Fe2As2 by naturally formed low-angle grain boundary networks

Josephson-like behavior in YBa$_2$Cu$_3$O$_{7-δ}$ nano-bridges carrying the depairing current

Transport Properties of Tl2Ba2CaCu2O8 Microbridges on a Low-Angle Step Substrate

Quasiparticle Heat Transport In Single-Crystalline Ba(1-X)Kxfe(2)As(2): Evidence For A K-Dependent Superconducting Gap Without Nodes

Impurity Effects on the Normal-State Transport Properties Ofba0.5k0.5fe2as2superconductors

Large and significantly anisotropic critical current density induced by planar defects in CaKFe4As4 single crystals

Transport properties, upper critical field and anisotropy of Ba(Fe 0.75 Ru 0.25 ) 2 As 2 single crystals