Abstract:We report exchange bias (EB) in single-phase CoO nanoparticles, where two magnetic phases naturally emerge as the crystallite size decreases from 34.6 to 10.8 nm. The Néel temperature (TN) associated with antiferromagnetic ordering decreases monotonically with the reduction in crystallite size, highlighting the significant influence of size effects. The 34.6 nm nanoparticles exhibit magnetization irreversibility between zero field cooled (ZFC) and field-cooled (FC) states below TN. This irreversibility appears well above TN with further reduction in size, resulting in the absence of true paramagnetic regime which indicates the occurrence of an additional magnetic phase. The frequency-dependent ac-susceptibility in 10.8 nm nanoparticles suggests slow dynamics of disordered surface spins above TN, coinciding with the establishment of long-range order in the core. The thermoremanent magnetization (TRM) and isothermoremanent magnetization (IRM) curves suggest a core-shell structure: the core is antiferromagnetic, and the shell consists of disordered surface spins causing ferromagnetic interaction. Hence, the exchange bias in these CoO nanoparticles results from the exchange coupling between an antiferromagnetic core and a disordered shell that exhibits unconventional surface spin characteristics.

Exchange Bias of CoO1−δ/(NiFe,Fe) System with Blocking Temperature Beyond Néel Temperature of Bulk CoO

Exchange Bias in (110)-Orientated Bi0.9la0.1feo3/La0.5ca0.5mno3 Films

Room-temperature Electric Control of Exchange Bias Effect in CoO1 – Δ/co Films Using Pb(Mg1/3Nb2/3)0.7Ti0.3O3 (110) Substrates

Room-temperature electric control of exchange bias effect in CoO<sub>1 – δ</sub>/Co films using Pb(Mg<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.7</sub>Ti<sub>0.3</sub>O<sub>3</sub> (110) substrates*

Enhanced exchange bias in MnN/CoFe bilayers after high-temperature annealing

Controlling exchange bias in Co-CoOx nanoparticles by oxygen content

Exchange Bias Effect and Magnetic Properties in ${\Hbox{la}}_{0.7}{\hbox{sr}}_{0.3}{\hbox{mno}}_{3}\hbox{-}{\Hbox{nio}}$ Nanocomposite Films

Exchange Bias in Co/CoO Core-Shell Nanowires: Roles of Antifer-Romagnetic Grain Size Distribution and Interfacial Spin Glass

Giant Exchange Bias and Ferromagnetism in the CoO Shell of Co/CoO-MgO Core-Shell Nanoparticles

Exchange Bias in Tetragonal-Like BiFeO3/Sr2FeMoO6 Bilayer

Exchange bias in (1 1 0)-orientated Bi 0.9La 0.1FeO 3/La 0.5Ca 0.5MnO 3 films

Exchange Bias and Its Thermal Stability in Ferromagnetic/antiferromagnetic Antidot Arrays

Unusual positive exchange bias after Zero-Field cooling at room temperature in the Co-CoO film composed of amorphous Co + CoO and crystallized Co/CoO

Fabrication of Co/CoO Exchange Bias System by Ion Implantation and Its Magnetic Properties

Influence of Atomic Roughness at the Uncompensated Fe/CoO(111) Interface on the Exchange-Bias Effect

Ferromagnetism And Exchange Bias In A Diluted Magnetic Ferroelectric Oxide

Size-induced Exchange Bias in Single-phase CoO Nanoparticles

Influence of Atomic Roughness at The Uncompensated Fe/CoO (111) Interface on Exchange Bias Effect

Giant exchange bias induced via tuning interfacial spins in polycrystalline Fe 3 O 4 /CoO bilayers

Large Exchange Bias and Enhanced Coercivity in Strongly-Coupled Ni/NiO Binary Nanoparticles

Giant Exchange Bias by Tuning Co/CoO Core/shell Structure