Abstract:Platinum-based catalysts are widely used for efficient catalysis of the acidic oxygen reduction reaction (ORR). However, the agglomeration and leaching of metallic Pt nanoparticles limit the catalytic activity and durability of the catalysts and restrict their large-scale commercialization. Therefore, this study aimed to achieve a uniform distribution and strong anchoring of Pt nanoparticles on a carbon support and improve the ORR activity and durability of proton-exchange membrane fuel cells. Herein, we report on the facile one-pot synthesis of a novel ORR catalyst using metal–nitrogen–carbon (M–N–C) bonding, which is formed in situ during the ion exchange and pyrolysis processes. An ion-exchange resin was used as the carbon source containing R-N+(CH3)3 groups, which coordinate with PtCl62− to form nanosized Pt clusters confined within the macroporous framework. After pyrolysis, strong M-N-C bonds were formed, thereby preventing the leaching and aggregation of Pt nanoparticles. The as-synthesized Pt supported on the N-doped hierarchically porous carbon catalyst (Pt/NHPC-800) showed high specific activity (0.3 mA cm−2) and mass activity (0.165 A mgPt−1), which are approximately 2.7 and 1.5 times higher than those of commercial Pt/C, respectively. The electrochemical surface area of Pt/NHPC-800 remained unchanged (~1% loss) after an accelerated durability test of 10,000 cycles. The mass activity loss after ADT of Pt/NHPC-800 was 18%, which is considerably lower than that of commercial Pt/C (43%). Thus, a novel ORR catalyst with highly accessible and homogeneously dispersed Pt-N-C sites, high activity, and durability was successfully prepared via one-pot synthesis. This facile and scalable synthesis strategy for high-efficiency catalysts guides the further synthesis of commercially available ORR catalysts.

One-Step Synthesis of Carbon-Supported Foam-Like Platinum with Enhanced Activity and Durability

Graphene Supported Foam-Like Platinum Electrocatalyst for Oxygen Reduction Reaction

Controlled Synthesis of High Metal-Loading, Pt-based Electrocatalysts with Enhanced Activity and Durability Toward Oxygen Reduction Reaction

Facile One-Pot Synthesis of Pd@Pt1L Octahedra with Enhanced Activity and Durability toward Oxygen Reduction

Optimized porous nanostructure of carbon fibers enabling excellent stability of Pt-based catalysts for oxygen reduction reaction

Facile Synthesis of Surfactant-Induced Platinum Nanospheres with a Porous Network Structure for Highly Effective Oxygen Reduction Catalysis

Enhanced stability and activity of platinum-based catalyst using iron-nitrogen co-doped graphene as support for oxygen reduction reaction

Synthesis of Platinum Nanocrystals Dispersed on Nitrogen-Doped Hierarchically Porous Carbon with Enhanced Oxygen Reduction Reaction Activity and Durability

Gram-scale synthesis of alkoxide-derived nitrogen-doped carbon foam as a support for Fe–N–C electrocatalysts

Oxygen Reduction Catalyzed by Pt Nanoparticles Confined in Mesoporous Carbon Supports Doped with Single Fe Atoms

Osmotic Pressure-Induced Pocket-Like Spheres With Fe Single-Atom Sites For The Oxygen Reduction Reaction

An elegant 3D-ordered hierarchically porous framework to anchor Pt nanocrystals for durable oxygen reduction reaction

A sulfur‐modified pore‐blocking method to enhance the electrocatalytic stability of carbon‐supported platinum nanoparticles

Cross-linked Multi-Atom Pt Catalyst for Highly Efficient Oxygen Reduction Catalysis

Selenium-Functionalized Carbon as a Support for Platinum Nanoparticles with Improved Electrochemical Properties for the Oxygen Reduction Reaction and CO Tolerance

Morphology engineering of self-assembled bimetallic PtCo alloy nanofoams as efficient multifunctional electrocatalysts for oxygen reduction and alcohol oxidation

Facile Synthesis of Nanoporous Pt‐Encapsulated Ir Black as a Bifunctional Oxygen Catalyst via Modified Polyol Process at Room Temperature

One-Step Synthesized Pt-on-NiCo Nanostructures for Oxygen Reduction with High Activity and Long-Term Stability

Surfactant-Guided Synthesis of Porous Pt Shells with Ordered Tangential Channels, Coated on Pd Nanostructures, and Their Enhanced Catalytic Activities.

One-pot facile synthesis of PtCu coated nanoporous gold with unique catalytic activity toward the oxygen reduction reaction

Fiber-Like Nanostructured Ti4o7 Used As Durable Fuel Cell Catalyst Support in Oxygen Reduction Catalysis