Abstract:To explore efficient non-noble metal-based electrocatalysts for oxygen reduction reaction (ORR), herein we developed a facile bottom-up approach for the fabrication of a hollow porous carbon sphere codoped with ultrasmall Co nanoparticles and uniform nitrogen distribution (Co-HNCS) via one-step pyrolysis of a core-shell type precursor composing of polystyrene (PS) core and bimetallic ZIF (zeolite imidazolate framework) shell. The bimetallic Co-Zn-ZIFs (BMZIFs) was selected as the sacrifice template due to not only its high nitrogen content and regular porosity but also the superiority that Zn species in BMZIFs can both spatially separate Co species to suppress the aggregation of ultra-small Co NPs and be evaporated to afford extra pores during high-temperature pyrolysis. As expected, by adjusting the starting molar ratio of Zn to Co, we were able to prepare Co-HNCS-x (x represent the molar ratio of Co to total starting metal feeding) that exhibited unique hollow structure with large surface areas, enhanced mass transport, high porosities, tunable particle sizes and graphitization degrees, abundant highly active CoNx sites, and thus significantly improved ORR performance. Particularly, the optimal Co-HNCS-0.2 exhibited the remarkable ORR activity (the onset and half-wave potentials were 0.94 and 0.82 V vs. RHE, respectively) via an efficient four-electron-dominant ORR process in alkaline medium, which outperformed that of commercial Pt/C (20 wt%, the onset and half-wave potentials were 0.93 and 0.80 V vs. RHE, respectively) and most of previously reported Co-based catalysts. Moreover, it also displayed much superior stability and tolerance to methanol as compared to Pt/C, further highlighting the merit of this facile synthesis approach. Our findings might inspire new thoughts on the development of precious-metal-free, highly-efficient and cost-effective ORR electrocatalysts derived from MOF.

Osmotic Pressure-Induced Pocket-Like Spheres With Fe Single-Atom Sites For The Oxygen Reduction Reaction

Iron, Nitrogen Co‐Doped Carbon Spheres As Low Cost, Scalable Electrocatalysts for the Oxygen Reduction Reaction

Precisely Designed Morphology and Surface Chemical Structure of Fe-N-C Electrocatalysts for Enhanced Oxygen Reaction Reduction Activity

Electrocatalytic Performance of Fe–N Encapsulated in Hollowly Mesoporous Carbon Microspheres for Oxygen Reduction Reaction and Zn–Air Battery

Fe-Based Metal Organic Framework-Derived FeNiP/N-Doped Carbon Heterogeneous Core-Shell Structures for Oxygen Evolution

Hierarchically porous Fe/N/S/C nanospheres with high-content of Fe-Nx for enhanced ORR and Zn-air battery performance

Formulating N‐Doped Carbon Hollow Nanospheres with Highly Accessible Through‐Pores to Isolate Fe Single‐Atoms for Efficient Oxygen Reduction

Template-assisted formation of atomically dispersed iron anchoring on nitrogen-doped porous carbon matrix for efficient oxygen reduction

Fe Single Atoms Anchored on N-doped Mesoporous Carbon Microspheres for Promoted Oxygen Reduction Reaction

Atomically Dispersed Fe/N4 and Ni/N4 Sites on Separate-Sides of Porous Carbon Nanosheets with Janus Structure for Selective Oxygen Electrocatalysis

Large-scale production of holey carbon nanosheets implanted with atomically dispersed Fe sites for boosting oxygen reduction electrocatalysis

Regulating the coordination environment of atomically dispersed Fe-N 4 moieties in carbon enables efficient oxygen reduction for Zn-air batteries

Simultaneously Engineering the Coordination Environment and Pore Architecture of Metal–Organic Framework‐Derived Single‐Atomic Iron Catalysts for Ultraefficient Oxygen Reduction

Porous Nanosheet Composite with Multi-Type Active Centers As an Efficient and Stable Oxygen Electrocatalyst in Alkaline and Acid Conditions

Breaking the N-limitation with N-enriched porous submicron carbon spheres anchored Fe single-atom catalyst for superior oxygen reduction reaction and Zn-air batteries

Asymmetric N, P‐Coordinated Single‐Atomic Fe Sites with Fe2P Nanoclusters/Nanoparticles on Porous Carbon Nanosheets for Highly Efficient Oxygen Electroreduction

Boosting Oxygen Reduction Catalysis with Fe–N4 Sites Decorated Porous Carbons Toward Fuel Cells

Engineering Molecular Heterostructured Catalyst for Oxygen Reduction Reaction

Self‐Sacrificing Template Synthesis of Carbon Nanosheets Assembled Hollow Spheres with Abundant Active Fe–N 4 O 1 Moieties for Electrocatalytic Oxygen Reduction

Collaborative integration of Fe-Nx active center into defective sulfur/selenium-doped carbon for efficient oxygen electrocatalysts in liquid and flexible Zn-air batteries

Rational Design of Hollow N/Co-doped Carbon Spheres from Bimetal-Zifs for High-Efficiency Electrocatalysis