Abstract:Core-shell structured carbon nanofiber@metal oxide is one of the most promising hybrid electrodes as supercapacitors, in which the pseudocapacitive metal oxides can be fully exerted and stabilized on the carbonaceous scaffolds. However, facile fabrication of mesoporous carbon nanofibers and integration of them with metal oxides are challenging. Herein, we report a new type of mesoporous carbon nanofibets (MCNs), derived from zinc-trimesic acid fibers, acting as the scaffolds to anchor nickel cobaltite (NiCo2O4) nanosheets after surface O-functionalization. The resultant core-shell OMCN@NiCo2O4 nanostructure is demonstrated by scanning electron microscope (SEM), elemental mapping, bright-field/highresolution transmission electron microscope (TEM), selected area electron diffraction (SAED) studies. The anchored NiCo2O4 nanosheets are dense (97.4%), and have a strong interaction with OMCN, as revealed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA) and H2-temperature programmed reduction (H-2-TPR) techniques. As expected, the OMCN@NiCo2O4 is highly efficient, showing a high specific capacitance of 1631 F g(-1) at the current density of 1 A g(-1), excellent rate capability and superior cycling stability up to 5000 cycles within a high capacitance retention ratio of 94.5%. This research opens the avenue to fabricate high-efficiency carbon-metal oxide electrodes using metal-organic framework fiber-derived mesoporous carbon nanofibers and integration of them with NiCo2O4 nanosheets by increasing the interfacial interaction. (C) 2018 Elsevier Inc. All rights reserved.

Preparation of porous (Ni,Co)3(BO3)2/Ni(OH)2 nanosheet networks as pseudocapacitor materials with superior performance

A Few Atoms Thick Nickel–Cobalt Oxides Mesoporous Nanosheets and Their Arrays on Ni Foam for Supercapacitors with Ultra-Long Cycling Lifespan

One-Pot Synthesis Of Porous Nickel Cobalt Sulphides: Tuning The Composition For Superior Pseudocapacitance

NiCo2S4 porous nanotubes synthesis via sacrificial templates: High-performance electrode materials of supercapacitors

Hierarchical Configuration of NiCo2S4 Nanotube@Ni–Mn Layered Double Hydroxide Arrays/Three-Dimensional Graphene Sponge As Electrode Materials for High-Capacitance Supercapacitors

Self-assembled Three-Dimensional Hierarchical CoMoO4 Nanosheets on NiCo2O4 for High-Performance Supercapacitor

Design of mesoporous Ni-Co hydroxides nanosheets stabilized by BO2- for pseudocapacitors with superior performance

Nickel–Cobalt Hydroxide Microspheres Electrodepositioned on Nickel Cobaltite Nanowires Grown on Ni Foam for High-Performance Pseudocapacitors

NiO/NixCo3-xO4 Porous Ultrathin Nanosheet/nanowire Composite Structures As High-Performance Supercapacitor Electrodes

Hierarchical NiCo2O4 Nanosheets@halloysite Nanotubes with Ultrahigh Capacitance and Long Cycle Stability As Electrochemical Pseudocapacitor Materials

3D Hierarchical Ni/NiCo2O4 Core-Shell Nanotube Arrays with High Capacitance and Stable Cycling Performance for Supercapacitor

Preparation of the Porous CoMoO4+NiMoO4 nanosheets with high capacitance by a Sol-gel method and freezing method

Supercapacitor performance of porous nickel cobaltite nanosheets

NiMoO4 Nanorods@hydrous NiMoO4 Nanosheets Core-Shell Structured Arrays for Pseudocapacitor Application

Preparation of Mesoporous Nio with Excellent Pseudocapacitive Behavior

The preparation of hierarchical tubular structures comprised of NiO nanosheets with enhanced supercapacitive performance

Ultrathin Β-Ni(oh)2 Nanoplates Vertically Grown on Nickel-Coated Carbon Nanotubes As High-Performance Pseudocapacitor Electrode Materials.

Formation of CMK-3/Co 3 O 4 Nanosheets on Nickel Foam with Markedly Enhanced Pseudocapacitive Properties

Self-Templated Synthesis of Porous Ni(OH)(2) Nanocube and Its High Electrochemical Performance for Supercapacitor

Nickel Cobaltite Nanosheets Coated on Metal-Organic Framework-Derived Mesoporous Carbon Nanofibers for High-Performance Pseudocapacitors.

Facile preparation of porous sheet-sheet hierarchical nanostructure NiO/Ni-Co-Mn-O x with enhanced specific capacity and cycling stability for high performance supercapacitors