Effects of Mn Substitution on Crystal Structure, Magnetic and Magnetocaloric Properties of (co1−xmnx)2b Compounds
D. Wang,L. Ma,G. H. Rao,J. Wang,X. Zhang,Y. B. Guo,L. Li
DOI: https://doi.org/10.1088/2053-1591/aa912c
IF: 2.025
2017-01-01
Materials Research Express
Abstract:The crystal structure, magnetic and magnetocaloric properties of (Co1-xMnx) 2B (x = 0.0, 0.1, 0.2, 0.25, 0.3, 0.35, 0.40) compounds were investigated by x-ray powder diffraction (XRD) and magnetization measurements. All compounds crystallize in a body-centred tetragonal single phase with the CuAl2-type structure. Due to the changes of lattice stability and ferromagnetic-antiferromagnetic exchange coupling interaction, the room temperature magnetization and the Curie temperature (TC) of (Co1-xMnx) 2B compounds first increases at about x = 0.1 and then decreases with the substitution of Mn for Co. Second-order phase transition was confirmed based on the isothermal magnetization curves and the isothermal entropy change (Delta SM) was determined for the samples with x = 0.3, 0.35 and 0.4. The maximal magnetic entropy (|Delta SM|) under a field change from 0 to 5 T are found to be 2.49, 2.37 and 2.02 J kg(-1) K for x = 0.3, 0.35 and 0.4, respectively. The corresponding relative cooling powers (RCP) are evaluated to be 59.74, 78.94 and 113.50 J kg(-1). Given the low cost of Co, Mn and B, (Co1-xMnx) 2B compounds may come as an base compound for a more efficient magnetocaloric material.