Abstract:The microstructures of precursors strongly affect the electrochemical performance of Ni-rich layer-structured cathode materials. In this study, the growth behaviour of Ni0.815Co0.15Al0.035(OH)2 (NCA) prepared via the ammonia complexation precipitation method in a 50-L-volume continuously stirred tank reactor (CSTR) is studied in detail. The growth of Ni(OH)2-based hydroxide can be divided into a nucleation process, an agglomeration growth process, a process in which multiple growth mechanisms coexist, and an interface growth process over time, while the inner structure of the CSTR can be divided into a nucleation zone, a complex dissolution zone, a growth zone, and a maturation zone. The concentration of ammonium ions affects the growth habit of the primary crystal significantly due to its specific adsorption on the electronegative crystal plane. When the ammonia concentration is <1.5 mol L−1 at 60 °C at pH = 11.5, the precursors grow preferentially along the (101) crystal plane, whereas they grow preferentially along the (001) crystal plane when the concentration is >2.0 mol L−1. The LiNi0.815Co0.15Al0.035O2 materials inherit the grain structure of the precursor. Materials prepared from precursors with (101) preferential primary particles show a higher specific capacity and better rate performance than those that were prepared from (001) preferential primary particles, but the latter realize a better cycling performance than the former.

Growth Mechanisms for Spherical Mixed Hydroxide Agglomerates Prepared by Co-Precipitation Method: A Case of Ni1/3co1/3mn1/3(Oh)(2)

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

Analysis of the growth mechanism of hierarchical structure Ni0.8Co0.1Mn0.1(OH)2 agglomerates as precursors of LiNi0.8Co0.1Mn0.1O2 in the presence of aqueous ammonia

Growth mechanisms for spherical Ni0.815Co0.15Al0.035(OH)2 precursors prepared via the ammonia complexation precipitation method

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Investigating the effect of pH on the growth of coprecipitated Ni0.8Co0.1Mn0.1(OH)2 agglomerates as precursors of cathode materials for Li-ion batteries

Formation of dispersive NiO nano-particles via hydrothermal modification

Synthesis the Precursor of LiNi0.5Mn0.5O2 Via an Improved Carbonate Co-Precipitation

Controllable Hydrothermal Conversion from Ni-Co-Mn Carbonate Nanoparticles to Microspheres

Preparation and Mechanism of Spherical [Ni<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>]Ox Precursors for Li [Ni<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>]O<sub>2</sub> by an Ultrasonic Atomization Method

Microstructure and Electrochemical Characterization of Spherical-Like Orthorhombic LiMnO2 Via Co-Precipitation

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Synthesis and Characterization of Spherical LiNi_(0.8)Co_(0.1)Mn_(0.1)O_2 Particles with a High Tap-density

Preparation and mechanism of spherical [Ni1/3Co1/3Mn1/3]OX precursors for Li[Ni1/3Co1/3Mn1/3]O2 by an ultrasonic atomization method

Co-precipitated Ni/Mn Shell Coated Nano Cu-rich Core Structure: A Phase-Field Study

Morphology-controlled Hydrothermal Synthesis and Growth Mechanism of Microcrystal Cu2O

Hydrothermal Growth and Structural Characterization of Ni(OH)2 Nanocrystals

The Crystal Growth Habits and Nucleation Mechanism of Hydrothermal Crystallization of Nano-AlOOH

Coordination polyhedra: A probable basic growth unit in solution for the crystal growth of inorganic nonmetallic nanomaterials?

The Preparation And The High-Temperature Properties Of The Spherical Ni(Oh)(2) Coated With Y(Oh)(3)

Insights into the Inner Structure of High-Nickel Agglomerate As High-Performance Lithium-Ion Cathodes