First-principles calculations of perpendicular magnetic anisotropy in Fe 1− x Co x /MgO(001) thin films
Guanzhi Cai,Zhiming Wu,Fei Guo,Yaping Wu,Heng Li,Qianwen Liu,Mingming Fu,Ting Chen,Junyong Kang
DOI: https://doi.org/10.1186/s11671-015-0825-3
2015-01-01
Nanoscale Research Letters
Abstract:The perpendicular magnetic anisotropy (PMA) of Fe 1− x Co x thin films on MgO(001) was investigated via first-principles density-functional calculations. Four different configurations were considered based on their ground states: Fe/MgO, Fe 12 Co 4 /MgO, Fe 10 Co 6 /MgO, and Fe 8 Co 8 /MgO. As the Co composition increases, the amplitude of PMA increases first from Fe/MgO to Fe 12 Co 4 /MgO, and then decreases in Fe 10 Co 6 /MgO; finally, the magnetic anisotropy becomes horizontal in Fe 8 Co 8 /MgO. Analysis based on the second-order perturbation of the spin-orbit interaction was carried out to illustrate the contributions from Fe and Co atoms to PMA, and the differential charge density was calculated to give an intuitive comparison of 3 d orbital occupancy. The enhanced PMA in Fe 12 Co 4 /MgO is ascribed to the optimized combination of occupied and unoccupied 3 d states around the Fermi energy from both interface Fe and Co atoms, while the weaker PMA in Fe 10 Co 6 /MgO is mainly attributed to the modulation of the interface Co- d xy orbital around the Fermi energy. By adjusting the Co composition in Fe 1− x Co x , the density of states of transitional metal atoms will be modulated to optimize PMA for future high-density memory application.