Low Hysteresis and Large Room Temperature Magnetocaloric Effect of Gd5Si2.05−xGe1.95−xNi2x (2x = 0.08, 0.1) Alloys

X. C. Zhong,J. X. Min,Z. W. Liu,Z. G. Zheng,D. C. Zeng,V. Franco,R. V. Ramanujan

DOI: https://doi.org/10.1063/1.4795434

IF: 2.877

2013-01-01

Journal of Applied Physics

Abstract:Gd5Si2.05−xGe1.95−xNi2x (2x = 0.08, 0.1) alloys were prepared by arc melting followed by annealing at 1273 K for 96 h. Mixed monoclinic Gd5Si2Ge2-type phase, orthorhombic Gd5Si4-type phase, and a small amount of Gd5Si3-type phase were obtained in these alloys. Gd5Si2.01Ge1.91Ni0.08 alloy undergoes a second-order transition (TC) around 300 K, whereas Gd5Si2Ge1.9Ni0.1 alloy exhibits two transitions including a first-order transition (TCІІ) at ∼295 K and second-order transition (TCІ) at ∼301 K. Ni substitution can effectively reduce the thermal hysteresis and magnetic hysteresis while maintaining large magnetic entropy change. The maximum magnetic entropy changes (|ΔSMmax|) of Gd5Si2.05−xGe1.95−xNi2x alloys with 2x = 0.08 and 0.1 are 4.4 and 5.0 J kg−1 K−1, respectively, for 0–2 T, and are 8.0 and 9.1 J kg−1 K−1, respectively, for 0–5 T. Low hysteresis performance and relatively large magnetic entropy change make these alloys favorable for magnetic refrigeration applications.