Interstitial nitrogen Atomic effect on the magnetic properties of Nd<sub>2</sub>Fe<sub>14</sub>B compound
Liang Zha,Zhongchong Lin,Fanggui Wang,Zhou Liu,Mingzhu Xue,Jie Yang,Wenyun Yang,Guang Tian,Jingzhi Han,Changsheng Wang,Honglin Du,Yingchang Yang,Jinbo Yang
DOI: https://doi.org/10.1016/j.jmmm.2020.167128
IF: 3.097
2020-01-01
Journal of Magnetism and Magnetic Materials
Abstract:The quaternary interstitial nitrides Nd2Fe14BN delta was synthesized through the gas-solid reaction of N-2 gas and Nd2Fe14B powders. It was found that Nd2Fe14BN delta alloy maintains the tetragonal structure (space group P4(2)/mnm) with an expansion of the unit cell. Structure analyses showed the nitrogen concentration (delta) is about 0.352(48) with the volume-expansion ratio (Delta V/V) of 0.6613% in the unit cell. Refinement of neutron diffraction data indicated that the N has a site occupation preference (8:3) for the 4e (0, 0, 0.0652) site over the 4f (0.1000, 0.1000, 0) site. The room temperature saturation magnetization and the magnetocrystalline anisotropy field of Nd2Fe14BN delta slightly decrease by about 6% and 5% as compared to the parent alloy, respectively. The Curie temperature of Nd2Fe14B compound increases from 312 degrees C to 331 degrees C after nitrogenation with such a subtle volume expansion, which provides a validation prediction that we may increase the volume-expansion ratio to improve T-c further. Therefore, Nd2Fe14BN delta, with better temperature stability could be obtained.