Abstract:The structural evolution and magnetic properties of nanostructured copper ferrite, CuFe2O4, have been investigated by x-ray diffraction, Mossbauer spectroscopy, and magnetization measurements. Nanometre-sized CuFe2O4 particles with a partially inverted spinel structure were synthesized by high-energy ball milling in an open container with grain sizes ranging from 9 to 61 nm. Superparamagnetic relaxation effects have been observed in milled samples at room temperature by Mossbauer and magnetization measurements. At 15 K, the average hyperfine held of CuFe2O4 decreases with decreasing average grain size while the coercive force, shift of the hysteresis loop, magnetic hardness, and saturation magnetization at 4.2 K increase with decreasing average grain size. At 295 K the coercive-held dependence on the average grain size is described, with particles showing superparamagnetic relaxation effects. At 4.2 K the relationship between the coercive field and average grain size can be attributed to the change of the effective anisotropy constant of the particles. The interface anisotropy of nanostructured CuFe2O4 is found to be about 1.8(1) x 10(5) erg cm(-3). Although spin canting was present, approximately 20% enhancement of the saturation magnetization in CuFe2O4 nanoparticles was observed, which could be explained by a cation redistribution induced by milling. The high-held magnetization irreversibility and shift of the hysteresis loop detected in our samples have been assigned to a spin-disordered phase, which has a spin-freezing temperature of approximately 50 K.

Magnetic and Structural Studies of the Verwey Transition in Fe3−δO4 Nanoparticles

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Structural Stability and Magnetism of Γ′-Fe4n and CoFe3N Compounds

Modulating the Verwey Transition of Epitaxial Magnetite Thin Films by Ionic Gating

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Magnetic and Mossbauer Studies on Oxygen Deficient Perovskite, La0.6sr0.4feo3-Delta

Magnetic Properties of Nanostructured Cufe2o4

Disappearing of the Verwey Transition in Magnetite Nanoparticles Synthesized under a Magnetic Field: Implications for the Origin of Charge Ordering

Magnetic order and ice rules in the multiferroic spinel FeV2O4

Structural Characterization and Tuning of Magnetic Properties of CoVδFe2-δO4 (0.0 ≤ δ ≤ 0.9) Nanomaterials Synthesized by Modified Sol-gel Autocombustion Method

Magnetism and Phase Transition for CoFe2−xMnxO4 Nanocrystalline Thin Films and Powders

Cation Ratio and Oxygen Defects for Engineering the Magnetic Transition of Monodisperse Nonstoichiometric Zinc Ferrite Nanoparticles

Neutron diffraction study of spin and charge ordering in SrFeO(3-delta)

Vacancy-driven non-cubic local structure and magnetic anisotropy tailoring in Fe$_x$O-Fe$_{3-δ}$O$_4$ nanocrystals

Structure and Magnetic Properties of MgFe2O4 Nanoparticles Prepared by the Low-Temperature Solid-State Reaction Method

Fine Structure and Magnetic Properties of Mn- and Co-doped Nanocrystalline Γ-Fe2o3

Probing low temperature non-equilibrium magnetic state in Co$_{2.75}$Fe$_{0.25}$O$_{4+δ}$ spinel oxide using dc magnetization, ac susceptibility and neutron diffraction experiments

Magnetic, Electronic and Structural Properties of ZnxFe3−xO4

Structure, magnetization and Mössbauer study of nanostructured Ni<sub>0.5</sub>Zn<sub>0.5</sub>Fe<sub>2</sub>O<sub>4</sub> ferrite powders

Size Dependence of Metal-Insulator Transition in Stoichiometric Fe3O4 Nanocrystals

Improving the magnetic and dielectric properties of Cu1−Ho FeO2 nanoceramics by tuning the vacancy defects and Fe valence state