Abstract:The Er3+-doped Al2O3 films were prepared by sintering Er-ion-implanted γ-AlOOH xerogel films on SiO2/Si(100) substrates. In a cycle, the γ-AlOOH xerogel films about 50 nm thick were dip-coated using aluminium isopropoxide-derived γ-AlOOH sols; the Er ions were then implanted into the γ-AlOOH xerogel films using an ion energy of 45 keV with different doses of 5×1014 to 1×1016 ions cm−2. Er3+-doped Al2O3 films were formed after 1, 2, and 4 cycles of dip-coating and implantation at different sintering temperatures of 800–1200 °C. The photoluminescence (PL) spectra were observed with a main peak at 1.533 μm and a side peak at 1.549 μm for all the Er3+-doped Al2O3 films. The intensity of PL peak of the Er3+-doped Al2O3 film obtained after 4 cycles with 5×1015 ions cm−2 dose at every cycle and sintered at 900 °C for 5 h, increased by about 10 and 3 times compared with that of the films obtained after 1 and 2 cycles. At the same sintering temperature of 900 °C, the intensity of PL peak of the Er3+-doped Al2O3 films first increased with the increase of dose from 5×1014 to 5×1015 ions cm−2 at every cycle, and then a saturation tendency was observed when the dose further was increased to 1×1016 ions cm−2. For the samples using 5×1015 ions cm−2 dose at every cycle, the PL intensity increased with the increase of sintering temperature from 800 to 1200 °C.

Photoluminescence Of Erbium Oxide Nanocrystals/Tio2/Gamma-Glycidoxypropyltrimethoxysilane (Glymo) Composite Sol-Gel Thin Films Derived At Low Temperature

Photoluminescence of Erbium Oxide Nanocrystals/tio2/γ-Glycidoxypropyltrimethoxysilane (GLYMO) Composite Sol–gel Thin Films Derived at Low Temperature

Photoluminescence characteristics of neodymium oxide nanocrystal/titania/ormosil composite sol-gel thin films

Structure and Photoluminescence of Ge Nanoparticles Embedded in SiO2 Gel Glasses Fabricated at Different Temperatures

Up-conversion Luminescence of Erbium (III) Oxalate Nanoparticles/titania/ÿ-Glycidoxypropyltrimethoxysilane Composite Sol-Gel Thin Films

Luminescence properties from erbium oxide nanocrystals dispersed in titania/organically modified silane composite sol–gel thin films

Visible Room-Temperature Photoluminescence of Ge-doped SiO2 Glasses Fabricated by a Sol–gel Process

Photoluminescence of Ge Nanoparticles Embedded in Sio2 Glasses Fabricated by A Sol-Gel Method

Preparation and Luminescence Properties of Neodymium(III) Oxide Nanocrystals Dispersed in Sol-gel Titania/ (Γ-Glycidoxypropyl)trimethoxysilane Composite Thin Films

Fluorescence characteristics from microemulsion technique derived erbium (III) oxide nanocrystals

Preparation and characterization of ultrafine neodymium oxide/TiO2/ORMOSIL sol-gel composite thin film

Luminescence Properties of Sol-Gel-Derived Organic-Inorganic Composite Films Dispersed with Erbium and Neodymium Oxalate Nanoparticles

Control of the Formation and Luminescent Properties of Polymorphic Erbium Silicates on Silicon

Electrophoretic Deposition and Photoluminescent Properties of Eu-doped BaTiO3thin Film from a Suspension of Monodispersed Nanocrystallites

Preparation and Up-Conversion Luminescence of Germania/γ-Glycidoxypropyltrimethoxysilane Organic–inorganic Hybrid Thin Films Dispersed with Neodymium Oxide Nanocrystals

Up-conversion luminescence of neodymium oxalate nanoparticles/TiO2/organically modified silane composite thin films derived at low temperature

Yellow-to-violet Upconversion in Neodymium Oxide Nanocrystal/titania/ormosil Composite Sol–gel Thin Films Derived at Low Temperature

Upconversion Luminescence Property of Er3+ and Yb3+ Co-doped Germanium Silicate Glass

Preparation And Characterization Of Erbium Doped Sol-Gel Silica Glasses

Effects of erbium oxalate content and temperature on green up-conversion luminescence of erbium oxalate nanoparticles/titania/ormosil composite thin films

Photoluminescence Properties of Er3+-doped Al2O3 Film Synthesized from Er-ion-implanted Γ-Alooh Xerogel