Abstract:Objectives: This study evaluated the phase composition, phase transformation behaviour, and mechanical properties of five heat-treated NiTi instruments. Methods: ProTaper NEXT (M-wire, PTN), ProTaper Gold (Gold-wire, PTG), One Curve (C-wire, OC), EdgeTaper Platinum (Fire-wire, ETP), NeoNiTi (electrical discharge machining-wire, NNA), and ProTaper Universal (conventional wire, PTU, control) with #25-tip size were tested (n = 12/group) for cyclic fatigue resistance (number of cycles to failure; NCF) and torsional resistance (angle of rotation to fracture and maximum torque at fracture [ultimate torsional strength]). The geometry and fracture surfaces of the tested instruments were examined by scanning electron microscopy. The phase transformation temperature and phase composition of the instruments were evaluated using differential scanning calorimetry and X-ray diffraction. Data were statistically analysed using one-way ANOVA and Tukey's post hoc test, with the significance level set at 5%. Results: PTG showed the highest NCF (P < .05) at 37°C, while ETP exhibited the highest angle of rotation to fracture, ultimate torsional strength, and stiffness (P < .05). Scanning electron microscopy demonstrated typical clusters of fatigue striations and numerous cracks after cyclic fatigue fracture, whereas there was a concentric abrasion pattern with a dimple and microvoids at the centre after torsional fracture. In differential scanning calorimetry curves, austenite-finishing temperatures of heat-treated instruments were higher than 37°C, whereas that of PTU was lower than 37°C. PTU showed strong peaks of austenite at 25 and 37°C, whereas ETP showed a strong peak of R-phase at 25°C, but mostly austenite phase at 37°C in X-ray diffraction. Conclusions: Geometry, alloy type, and phase transformation temperatures of NiTi instruments affected their mechanical behaviour. Clinical relevance: PTG showed the highest NCF, suitable for markedly curved canals. ETP had the highest torsional resistance, appropriate for narrow and constricted canals.

An Overview of the Mechanical Properties of Nickel–titanium Endodontic Instruments

Influence of Fluoride-Containing Acidic Artificial Saliva on the Mechanical Properties of Nickel-Titanium Orthodontics Wires.

Current Challenges and Concepts of the Thermomechanical Treatment of Nickel-Titanium Instruments

[Comparison of Mechanical Properties on Different Phase Transformation Points of Nickel-Titanium Orthodontic Wires].

Heat Treatment and Surface Treatment of Nickel–Titanium Endodontic Instruments

Nickel–titanium: options and challenges

Mechanical Properties of Controlled Memory and Superelastic Nickel-Titanium Wires Used in the Manufacture of Rotary Endodontic Instruments

Ultrasonic fatigue behavior of nickel-titanium endodontic instruments under flexural conditions

Comparative Study of Torsional and Bending Properties for Six Models of Nickel-Titanium Root Canal Instruments with Different Cross-Sections.

Mechanical properties of nickel-titanium endodontic instruments and the effect of sodium hypochlorite treatment

Nickel-titanium instruments for root canal preparation

VSL#3 Probiotic-Mixture Induces Remission in Patients with Active Ulcerative Colitis

MiR‐204, down‐regulated in retinoblastoma, regulates proliferation and invasion of human retinoblastoma cells by targeting CyclinD2 and MMP‐9

Phase Transformation and Mechanical Behaviour of Different Heat-Treated Nickel-Titanium Rotary Instruments

Fatigue Behavior of Ni-Ti Alloy Endodontic Files under Ultrasonic Unconstrained Condition

Torsion Property and Cyclic Fatigue Fracture Behavior of Nickel-Titanium Endodontic Instruments

Effects of R-Phase on Mechanical Responses of a Nickel-Titanium Endodontic Instrument: Structural Characterization and Finite Element Analysis

Phase Transformation Behavior and Mechanical Properties of Thermomechanically Treated K3xf Nickel-Titanium Instruments

Mechanical properties analysis of medical endodontic instruments based on parameterization

Transport of gatifloxacin involves Na+/Ca2+ exchange and excludes P-glycoprotein and multidrug resistance associated-proteins in primary cultured rat brain endothelial cells.

Comparative Analysis of NiTi Instruments with Different Alloy Treatments