Surface Modification of Mg Alloys AZ31 and ZK60-1Y by High Current Pulsed Electron Beam
Gao Bo,Hao Yi,Zhang Wenfeng,Tu Ganfeng
DOI: https://doi.org/10.5772/16808
2011-01-01
Abstract:IntroductionThe quality of Mg alloys with high specific modulus and specific strength is the lightest in the structural materials.Their density is about 2/3 of aluminium alloys and 1/4 of steels.The weight of whole structural materials is decreased drastically owing to some components or parts produced by Mg alloys.Thus, Mg alloys are widely used in aerospace, weapons, automobile and other fields [1][2][3].Meanwhile, Mg alloys has many other advantages, such as excellent electromagnetic shielding performance, shock absorption ability, electric and heat conductivity, etc [4][5][6].However, the chemical stability of Mg is very low, and its electrode potential is negative (-2.34V).As a result, the corrosion resistance of Mg alloys is poor in acid and neutral mediums.Furthermore, other properties of Mg alloys, wear resistance, hardness and resistance to high temperature, are also poor.Consequently, the superiority of Mg alloys in the application is restricted to some extent.Nowadays, the researches are concentrated on the improvement of hardness, wear and corrosion resistance of Mg alloys.Energy beam surface modification is an important developing direction, such as plasma micro-arc oxidation [7][8][9][10][11], laser surface treatment [12][13][14][15][16], ion beam surface modification [17][18][19], etc. A.V. Apelfeld et al [10] have studied oxide protective coatings on the surface of Mg alloys obtained by micro-arc oxidation (MAO).A model of micro-arc coating formation is proposed.For Mg alloys, the structure of MAO coating plays an important role in improvement of corrosion resistance.The research team (Y.M. Wang et al [11]) has investigated that dense oxide coatings formed in alkaline silicate electrolyte with and without titania sol addition are fabricated on AZ91D alloy using micro-arc oxidation.It reveals that the coating thickness decreases from 22µm to 18 µm with increasing concentration of titania sol from 0 to 10 vol.%.Electrochemical tests show that the Ecorr of Mg substrate positively shifts about 300-500 mV and Icorr lowers more than 100 times after micro-arc oxidation.The literature [15] (A.K. Mondal et al) has reported that Mg alloy ACM720 is subjected to laser surface treatment using Nd:YAG laser in argon atmosphere.This treatment is beneficial for enhancing the corrosion and wear resistance of the alloy.The improved corrosion resistance is attributed to the absence of second phase Al 2 Ca at the rain boundaries, microstructural refinement and extended solid solubility, particularly of Al, in (Mg) matrix owing to rapid solidification.The laser treatment also increases surface hardness two times and reduces the wear rate considerably due to grain refinement. www.intechopen.comSpecial Issues on Magnesium Alloys 26 J. Dutta Majumdar and I. Manna [16] have researched that the mechanical properties of laser-surface-alloyed AZ91, a magnesium-based alloy (Mg-9Al-0.9Zn)with nickel.Laser surface alloying is carried out using a continuous wave CO 2 laser.As a result, laser surface alloying leads to the formation of a dispersion of intermetallics of Mg and Ni (MgNi 2 ) in an Mg matrix with an improved Young's modulus (45-85 GPa, as compared to the 45 GPa of asreceived substrate) and improved wear resistance.J.X. Yang et al [19] have found that thin carbon nitride (CN) coating can be deposited on Mg alloy substrate by ion beam assisted deposition.Through adjusting parameter, the coating with high N/C ratio of 0.38 is produced.The CN coating is a composition of amorphous C 3 N 4 and improves the roughness of naked substrate from 32.9 nm to 28.9 nm.Moreover, the percentage increases of hardness and elastic modulus induced by coating are more than 90.6% and 82.8%, respectively.Surface treatment of electron beam on metallic materials, such as steels, pure Al and Al alloys, NiTi alloy, has recently been investigated by domestic and foreign researchers [20][21][22][23][24][25][26].It is found that metastable structures are formed on treated material surface and the hardness as well as wear and corrosion resistance is enhanced after electron beam treatment.However, the investigation on Mg alloys after electron beam treatment is reported rarely in literatures.In our group, the change in microstructure and properties of Mg alloys (AZ31, ZK60-1Y) has been researched in detail before and after HCPEB treatment.