Abstract:In this study, our primary aim was to increase the presence of amine groups in polyamide 6 fibers. To achieve this, we employed a functionalization process that mainly depended on increasing the number of reactive sites via acid-catalyzed hydrolysis. The effects of several acids were rigorously examined, including hydrochloric acid (HCl), sulfuric acid (H2SO4), and formic acid (HCOOH). Following this comprehensive acid-based treatment, the method that demonstrated the most significant increase in amine groups was selected for further evaluation in dyeing experiments and full characterization. The quantification of amino groups was performed using potentiometry, evaluating the equilibrium state of acid removal from the fibers. To corroborate these results, the acid dye Levaset Blue 2R was employed, which measured the amount of dye bound to the fibers during the dyeing process. Characterization of the polyamide 6 fiber structural changes was conducted using multiple techniques, including tensile tests, Fourier transform infrared (FTIR) spectroscopy, and differential scanning calorimetry (DSC). Among the acid treatments, the 11% HCl treatment exhibited the most significant increase in amine groups, amounting to an approximately 110% increase as measured by potentiometry and an approximately 150% increase using the dyeing method. During the dyeing process, the 11% HCl-treated fibers absorbed 91% of the dye from the dye bath, indicating enhanced color intensity and K/S value, thus affirming the efficacy of the amine group increasing. Tensile testing revealed a decrease in the strength of the functionalized fiber. In the FTIR spectra, there was a notable increase in the intensity of bands associated with the fiber's crystalline regions and hydrogen bonds. DSC tests validated the FTIR results, demonstrating a 9% increase in crystallinity. Furthermore, SEM micrographs depicted surface alterations induced by the hydrolysis process. These results collectively highlight the effectiveness of hydrolysis in introducing functional groups, enhancing color intensity during dyeing with acid dyes, and reducing dye content in the bath. Additionally, the potentiometric method for quantifying amine group demonstrated practicality and accuracy, serving as a valuable contribution to the field.

Study of Hydrophilic Modification for Polyamide 6,6 and Its Characterization

Surface Modification of Polyamide 6,6 Fabrics with an Alkaline Protease – Subtilisin

Microwave-initiated modification of polyamide 6.6 fabric surfaces for superior hydrophilic and flame retardant properties

Preparation and characterization of super hydrophobic aerogel coated ultra-high molecular weight polyethylene fabric

Surface modification of polyamide fabric based on a multi-enzyme system

Enhancing polyamide 6: Acid hydrolysis for functionalization and amino group quantification

Hydrophilic Modification of Polyester/Polyamide 6 Hollow Segmented Pie Microfiber Nonwovens by UV/TiO2/H2O2

Flame retardant and hydrophilic coatings on undyed and dyed polyamide 6.6 textiles: Clarifying the processing and performance

Investigation of stain-resistant cationic dyeable nylon 6 modified with sodium salt of 5-sulfoisophthalic acid and polyethylene glycol

Discussion on Factors Affecting Dyeing of Bio-based Polyamide 5,6 Fibers Compared with Polyamide 6,6 Fibers

Structure and Physical Properties of Hydrophilic Polyamide Copolymers Fiber Based on Nylon 6 and Nylon 4,6

A Lipid Coating on Cotton Fibers with Enhanced Adsorption Capability for Fabric Functionalization

Mechanical properties, moisture absorption, and dyeability of polyamide 5,6 fibers

Improving the hygroscopicity and flame retardancy of polyamide 6 fabrics by surface coating with β-FeOOH and sulfamic acid

Micro crystalline cellulose aided surface modification and deposition of green polyelectrolytes for the improved hydrophilicity and flame retardancy of polyamide 66 fabric

[Studies of human intestinal parasitism at Compodimele (Latina province)].

Flame retardant and anti-dripping modification of polyamide 6 fabric by guanidine sulfamate with enhanced durability

Few Layer Deposition and Sol-Gel Finishing of Organic-Inorganic Compounds for Improved Flame Retardant and Hydrophilic Properties of Polyamide 66 Textiles: A Hybrid Approach

Surface functionalization of polyamide fiber via dopamine polymerization

Synthesis and application of silicone-modified polyurethane as a slip-elastic finishing agent for polyamide fabrics

Nanoparticles Based Coatings for Multifunctional Polyamide 66 Textiles with Improved Flame Retardancy and Hydrophilicity