Dissolution characteristics of TiC0.3N0.7 in low-carbon and safe blast furnace hearth
Yanxiang Liu,Ziyu Guo,Jianliang Zhang,Kexin Jiao,Yanbing Zong,Cui Wang
DOI: https://doi.org/10.1051/metal/2024006
IF: 0.9461
2024-02-20
Metallurgical Research & Technology
Abstract:Investigating the presence of a Ti(C,N) protective layer in molten iron is of great significance for achieving low carbon and safe production in blast furnaces. This study focuses on analyzing the high temperature dissolution experiment of TiC 0.3N 0.7 in molten iron to elucidate the kinetics and mechanisms involved, as well as strategies for regulating its dissolution. The results reveal that the dissolution reaction of TiC 0.3N 0.7 is predominantly influenced by the temperature and flow speed of the molten iron. The dissolution process can be categorized into two stages: dissolution reaction and physical penetration. Diffusion mass transfer is the dominant factor controlling the dissolution of TiC 0.3N 0.7, with an apparent activation energy of 60.15 kJ/mol. Upon contact with molten iron, dendritic penetration of TiC 0.3N 0.7 particles occurs, starting from the edges. To enhance the stable presence of TiC 0.3N 0.7, recommendations include reinforcing furnace cylinder cooling, reducing the heat transfer coefficient of the blast furnace hearth's resistant material, increasing the carbon content of the molten iron, and decreasing the sulfur content of the molten iron.
metallurgy & metallurgical engineering