Structural and electrochemical properties of the La0.7Mg0.3Ni2.975-xCo0.525Mnx hydrogen storage electrode alloys
Hongge Pan,Yongfeng Liu,Mingxia Gao,Yunfeng Zhu,Yongquan Lei,Qidong Wang
DOI: https://doi.org/10.1149/1.1643070
IF: 3.9
2004-01-01
Journal of The Electrochemical Society
Abstract:The effect of partial substitution of Mn for Ni on the structural and electrochemical properties of the La 0.7 Mg 0.3 Ni 2975-x Co 0.525 Mn x (x = 0.0, 0,1, 0.2, 0.3, 0.4, 0.5) hydrogen storage alloys has been investigated systematically. The results of X-ray powder diffraction and Rietveld analyses showed that all alloys consisted of the (La, Mg)Ni 3 phase and the LaNi 5 phase, and the content of the (La, Mg)Ni 3 phase first remained unchanged (∼77 wt %) and then decreased, but the content of the LaNi 5 phase increased progressively with increasing x. Meanwhile, the lattice parameters and cell volumes of the ( La, Mg)Ni 3 phase and the LaNi 5 phase all increased with increasing Mn content. The pressure composition isotherms showed that the hydrogen storage capacity first remained almost unchanged and then decreased with increasing x from 0.0 to 0.5, and the equilibrium pressure decreased from 0.51 atm to 0.06 atm. The electrochemical measurements indicated that the maximum discharge capacity first remains unchanged (∼400 mAh/g) with increasing x from 0.0 to 0.2 and then decreased when x increased further. Moreover, the high rate discharge-ability, the exchange current density I 0 , the limiting current density I L , and the hydrogen diffusion coefficient D of the alloy electrodes all increased first and then decreased with increasing x, which indicates that the kinetics of hydriding/dehydriding of the La 0.7 Mg 0.3 Ni 2.975-x Co 0.525 Mn x (x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5) hydrogen storage alloys increased first up to x = 0.1 and then decreased with further increasing x.