Abstract:A cyclic inclined impact–sliding test was operated in an unlubricated, ambient environment and Hank's balanced salt solution (HBSS) to study the contact fatigue wear behavior of DLC and TiN biomedical coatings on relatively soft but corrosion resistant Ti alloy (Ti6Al4V) and hard but corrodible AISI M2 steel as model systems. The test was designed to simulate coating wear under combined impact and sliding motion. In each impact–sliding cycle, the forces comprised a dynamic impact load, Fi (140N) and a “pressing” load, Fp (300N). As expected, both coatings performed better on hard M2 substrates than Ti substrates under ambient test conditions. In the HBSS-lubricated solution test conditions, no obvious corrosion degradation occurred when either the bonding layers or substrates were Ti-based; instead, the solution provided a lubricating effect and enhanced coating performance. When the bonding layer for the DLC coating case was Si-based, it could not prevent crack propagation into the substrate after a certain number of test cycles. The crack opening allowed the HBSS solution to contact the substrates, which should only cause a minor problem when the substrate was a corrosion-resistant Ti alloy. However, when the substrate was corrodible M2, a severe corrosion-induced weakening of the interface occurred. When the coating bonding layer was a Ti layer (within the TiN coating), it could function to some extent as a corrosion and crack barrier to protect the M2 steel from interface degradation. Thus, a corrosion-resistant bonding layer and its ability to impede extension of cracking under cyclic dynamic loads can have a positive influence on the coating performance when the substrate has inferior anti-corrosion properties.

Study on fatigue and wear behaviors of a TiN coating using an inclined impact-sliding test

High Temperature Sliding Wear Behaviors of Ion Plating Tin Composite Coating with Ion Nitriding As Interlayer on Hot Work Die Steel

Tribological Behaviors of Spot-Textured TiN Coatings on M2 High-Speed Steel under Boundary Lubricated Conditions

Study of the Fatigue Wear Behaviors of a Tungsten Carbide Diamond-Like Carbon Coating on 316L Stainless Steel

A Method for Evaluating the Impact Wear Behavior of Multilayer TiN/Ti Coating

Estimation of fatigue life of TiN coatings using cyclic micro-impact testing

Effect of Triangular Texture on the Tribological Performance of Die Steel with Tin Coatings under Lubricated Sliding Condition

Substrate and bonding layer effects on performance of DLC and TiN biomedical coatings in Hank's solution under cyclic impact–sliding loads

Study on the Damage Mechanism of TiN/Ti Coatings Based on Multi-Directional Impact

Study on Failure Mechanisms of Dlc Coated Ti6al4v and Cocr under Cyclic High Combined Contact Stress

The Tribological Property and Microstructure of Ni-Ti Coating Prepared by Electrodeposition and Heat Treatment

Effects of Mechanical Properties and Layer Structure on the Cyclic Dynamic Loading of TiN-based Coatings

Tribological Properties of TiN/diamond and TiAlN/diamond Bilayer Films Sliding Against Carbon Steel

Effects of Different Substrates on Micromechanical and Tribology Properties of TiN Films

Load Sensitivity in Repetitive Nano-Impact Testing of TiN and AlTiN Coatings

Sliding friction and wear behaviour of ion nitrided and TiN coated AISI 4140 steel

Tribological Properties of Craln and Tin Coatings Tested in Nano- and Micro-Scale Laboratory Wear Tests

Tribological Behaviour of Nanostructured Al2O3-3 Wt% TiO2 Coating Against Steel in Dry Sliding

Friction and wear behavior of the PVD (Zr,Ti)N coated cemented carbide against 40Cr hardened steel

Deformation behavior and wear resistance of hard TiCN and TiCN/Ti coatings on Ti6Al4V alloy